Silicon implanted and annealed SiO2 layers are studied usin g photoluminescence (PL) and positron annihilation spectroscopy (PAS). Two PL emission bands are observed. a band centered at 560 nm is present in as-implanted samples and it is still observed after 1000 degrees C annealing. The emission time is fast. A second band centered at 780 nm is detected after 1000 degrees C annealing. The intensity of the 780 nm band further increased when hydrogen annealing was performed. The emission time is long (1 mu s to 0.2 ms). PAS results show that defects produced by implantation anneal at 600 degrees C. Based on the annealing behavior and on the emission times, the origin of the two bands is discussed.
Visible light emission from silicon implanted and annealed SiO2 layers / Ghislotti, G; Nielsen, B; Asokakumar, P; Lynn, Kg; Dimauro, Lf; Bottani, Ce; Corni, Federico; Tonini, Rita; Ottaviani, Giampiero. - In: JOURNAL OF THE ELECTROCHEMICAL SOCIETY. - ISSN 0013-4651. - STAMPA. - 144:(1997), pp. 2196-2199.
Visible light emission from silicon implanted and annealed SiO2 layers
CORNI, Federico;TONINI, Rita;OTTAVIANI, Giampiero
1997
Abstract
Silicon implanted and annealed SiO2 layers are studied usin g photoluminescence (PL) and positron annihilation spectroscopy (PAS). Two PL emission bands are observed. a band centered at 560 nm is present in as-implanted samples and it is still observed after 1000 degrees C annealing. The emission time is fast. A second band centered at 780 nm is detected after 1000 degrees C annealing. The intensity of the 780 nm band further increased when hydrogen annealing was performed. The emission time is long (1 mu s to 0.2 ms). PAS results show that defects produced by implantation anneal at 600 degrees C. Based on the annealing behavior and on the emission times, the origin of the two bands is discussed.
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris