Charge trapping study at 300 and 77 K in ferroelectric (annealed Al- or Si-doped) and nonferroelectric (unannealed and/or undoped) HfO2 films grown by atomic layer deposition reveals the presence of "deep"and "shallow"electron traps with volume concentrations in the 1019-cm-3 range. The concentration of deep traps responsible for electron trapping at 300 K is virtually insensitive to the oxide doping by Al or Si but slightly decreases in films crystallized by high-temperature annealing in oxygen-free ambient. This behavior indicates that the trapping sites are intrinsic and probably related to disorder in HfO2 rather than to the oxygen deficiency of the film. Electron injection at 77 K allowed us to fill shallow electron traps energetically distributed at ∼0.2 eV. These electrons are mobile and populate states with thermal ionization energies in the range ∼0.6-0.7 eV below the HfO2 conduction band (CB). The trap energy depth and marginal sensitivity of their concentration to crystallization annealing or film doping with Si or Al suggests that these traps are associated with boundaries between crystalline grains and interfaces between crystalline and amorphous regions in HfO2 films. This hypothesis is supported by density functional theory calculations of electron trapping at surfaces of monoclinic, tetragonal, and orthorhombic phases of HfO2. The calculated trap states are consistent with the observed thermal ionization (0.7-1.0 eV below the HfO2 CB) and photoionization energies (in the range of 2.0-3.5 eV below the HfO2 CB) and support their intrinsic polaronic nature.

Electron trapping in ferroelectric HfO2 / Izmailov, R. A.; Strand, J. W.; Larcher, L.; O'Sullivan, B. J.; Shluger, A. L.; Afanas'Ev, V. V.. - In: PHYSICAL REVIEW MATERIALS. - ISSN 2475-9953. - 5:3(2021), pp. 1-2. [10.1103/PhysRevMaterials.5.034415]

Electron trapping in ferroelectric HfO2

Strand J. W.;Larcher L.;
2021

Abstract

Charge trapping study at 300 and 77 K in ferroelectric (annealed Al- or Si-doped) and nonferroelectric (unannealed and/or undoped) HfO2 films grown by atomic layer deposition reveals the presence of "deep"and "shallow"electron traps with volume concentrations in the 1019-cm-3 range. The concentration of deep traps responsible for electron trapping at 300 K is virtually insensitive to the oxide doping by Al or Si but slightly decreases in films crystallized by high-temperature annealing in oxygen-free ambient. This behavior indicates that the trapping sites are intrinsic and probably related to disorder in HfO2 rather than to the oxygen deficiency of the film. Electron injection at 77 K allowed us to fill shallow electron traps energetically distributed at ∼0.2 eV. These electrons are mobile and populate states with thermal ionization energies in the range ∼0.6-0.7 eV below the HfO2 conduction band (CB). The trap energy depth and marginal sensitivity of their concentration to crystallization annealing or film doping with Si or Al suggests that these traps are associated with boundaries between crystalline grains and interfaces between crystalline and amorphous regions in HfO2 films. This hypothesis is supported by density functional theory calculations of electron trapping at surfaces of monoclinic, tetragonal, and orthorhombic phases of HfO2. The calculated trap states are consistent with the observed thermal ionization (0.7-1.0 eV below the HfO2 CB) and photoionization energies (in the range of 2.0-3.5 eV below the HfO2 CB) and support their intrinsic polaronic nature.
2021
5
3
1
2
Electron trapping in ferroelectric HfO2 / Izmailov, R. A.; Strand, J. W.; Larcher, L.; O'Sullivan, B. J.; Shluger, A. L.; Afanas'Ev, V. V.. - In: PHYSICAL REVIEW MATERIALS. - ISSN 2475-9953. - 5:3(2021), pp. 1-2. [10.1103/PhysRevMaterials.5.034415]
Izmailov, R. A.; Strand, J. W.; Larcher, L.; O'Sullivan, B. J.; Shluger, A. L.; Afanas'Ev, V. V.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1249291
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 10
social impact