An epoxy resin was nanomodified with in-situ generated silver nanoparticles (Ag) and with various amounts of carbon black (CB) and carbon nanofibers (NF), in order to increase the electrical conductivity of the matrix. Differential scanning calorimetry tests revealed how the addition of both CB and NF led to a slight decrease of the glass transition temperature of the material, while electron microscopy evidenced how the dimension of CB aggregates increased with the filler content. Both flexural modulus and stress at yield were decreased by CB addition, and the introduction of Ag nanoparticles promoted an interesting improvement of the flexural resistance. CB resulted to be more effective than NF in decreasing the electrical resistance of the materials down to 103 !·cm. Therefore, a rapid heating of the CB-filled samples upon voltage application was observed, while Ag nanoparticles allowed a stabilization of the temperature for elevated voltage application times.

Electrically conductive epoxy nanocomposites containing carbonaceous fillers and in-situ generated silver nanoparticles / A., Dorigato; G., Giusti; Bondioli, Federica; A., Pegoretti. - In: EXPRESS POLYMER LETTERS. - ISSN 1788-618X. - ELETTRONICO. - 7:8(2013), pp. 673-682. [10.3144/expresspolymlett.2013.64]

Electrically conductive epoxy nanocomposites containing carbonaceous fillers and in-situ generated silver nanoparticles

BONDIOLI, Federica;
2013

Abstract

An epoxy resin was nanomodified with in-situ generated silver nanoparticles (Ag) and with various amounts of carbon black (CB) and carbon nanofibers (NF), in order to increase the electrical conductivity of the matrix. Differential scanning calorimetry tests revealed how the addition of both CB and NF led to a slight decrease of the glass transition temperature of the material, while electron microscopy evidenced how the dimension of CB aggregates increased with the filler content. Both flexural modulus and stress at yield were decreased by CB addition, and the introduction of Ag nanoparticles promoted an interesting improvement of the flexural resistance. CB resulted to be more effective than NF in decreasing the electrical resistance of the materials down to 103 !·cm. Therefore, a rapid heating of the CB-filled samples upon voltage application was observed, while Ag nanoparticles allowed a stabilization of the temperature for elevated voltage application times.
2013
7
8
673
682
Electrically conductive epoxy nanocomposites containing carbonaceous fillers and in-situ generated silver nanoparticles / A., Dorigato; G., Giusti; Bondioli, Federica; A., Pegoretti. - In: EXPRESS POLYMER LETTERS. - ISSN 1788-618X. - ELETTRONICO. - 7:8(2013), pp. 673-682. [10.3144/expresspolymlett.2013.64]
A., Dorigato; G., Giusti; Bondioli, Federica; A., Pegoretti
File in questo prodotto:
File Dimensione Formato  
EPL-0004415_article.pdf

Open access

Tipologia: Versione pubblicata dall'editore
Dimensione 1.51 MB
Formato Adobe PDF
1.51 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/946091
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 21
  • ???jsp.display-item.citation.isi??? 20
social impact