The adsorption of Na onto GaP(110) is markedly different when the substrate is held below 120 K and above 140 K. At 120 K, the development of core and valence level photoemission spectra is consistent with charge transfer between the alkali metal and the surface atoms of a chemically undisrupted substrate. However, at 140 K, similar measurements show very different spectral changes, resembling more closely a reactive interface, involving interaction between the Na and bulk GaP atoms

Data di pubblicazione:	1994
Titolo:	Temperature-dependent growth of the Na/GaP(110) interface
Autore/i:	D. A., Evans; P., Bailey; J. M. C., Thornton; D'Addato, Sergio
Autore/i UNIMORE:	D. A. Evans P. Bailey J. M. C. Thornton D'ADDATO, Sergio mostra contributor esterni nascondi contributor esterni
Rivista:	SURFACE REVIEW AND LETTERS
Volume:	1
Pagina iniziale:	597
Pagina finale:	600
Citazione:	Temperature-dependent growth of the Na/GaP(110) interface / D. A., Evans; P., Bailey; J. M. C., Thornton; D'Addato, Sergio. - In: SURFACE REVIEW AND LETTERS. - ISSN 0218-625X. - STAMPA. - 1(1994), pp. 597-600.
Tipologia	Articolo su rivista

File in questo prodotto:

Non ci sono file associati a questo prodotto.

Utilizza questo identificativo per citare o creare un link a questo documento:
http://hdl.handle.net/11380/738056

Citazioni

I documenti presenti in Iris Unimore sono rilasciati con licenza Creative Commons Attribuzione - Non commerciale - Non opere derivate 3.0 Italia, salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris