Polyphase boride coatings constituted by an inner layer of Fe2B and an outer layer of FeB were thermochemically grown on iron andmedium carbon steel by a pack cementation process. The tribological behaviour of borided samples was investigated under both slidingand abrasion testing conditions. Considerably different values of wear rate were found in different regions of the coatings. The differenceswere explained on the basis of the crystallographic order of iron borides. The resistance to both types of wear was initially poor due tothe presence on the coatings of a thin, friable layer constituted by disordered crystals. Then the resistance increased to a maximum valuein regions constituted by compact, highly ordered crystals of Fe2B. The resistance to dry sliding of borided samples was better than thatdisplayed by samples submitted to alternative surface treatments (e.g. gas nitriding) and lower that that measured for aWC–Co hard metalcoating.

Sliding and abrasive wear behaviour of boride coatings / C., Martini; G., Palombarini; Poli, Giorgio; D., Prandstraller. - In: WEAR. - ISSN 0043-1648. - STAMPA. - 256:6(2004), pp. 608-613. [10.1016/j.wear.2003.10.003]

Sliding and abrasive wear behaviour of boride coatings

POLI, Giorgio;
2004

Abstract

Polyphase boride coatings constituted by an inner layer of Fe2B and an outer layer of FeB were thermochemically grown on iron andmedium carbon steel by a pack cementation process. The tribological behaviour of borided samples was investigated under both slidingand abrasion testing conditions. Considerably different values of wear rate were found in different regions of the coatings. The differenceswere explained on the basis of the crystallographic order of iron borides. The resistance to both types of wear was initially poor due tothe presence on the coatings of a thin, friable layer constituted by disordered crystals. Then the resistance increased to a maximum valuein regions constituted by compact, highly ordered crystals of Fe2B. The resistance to dry sliding of borided samples was better than thatdisplayed by samples submitted to alternative surface treatments (e.g. gas nitriding) and lower that that measured for aWC–Co hard metalcoating.
2004
256
6
608
613
Sliding and abrasive wear behaviour of boride coatings / C., Martini; G., Palombarini; Poli, Giorgio; D., Prandstraller. - In: WEAR. - ISSN 0043-1648. - STAMPA. - 256:6(2004), pp. 608-613. [10.1016/j.wear.2003.10.003]
C., Martini; G., Palombarini; Poli, Giorgio; D., Prandstraller
File in questo prodotto:
File Dimensione Formato  
Sliding and abrasive wear behaviour of boride coatings.pdf

Accesso riservato

Tipologia: Versione dell'autore revisionata e accettata per la pubblicazione
Dimensione 208.02 kB
Formato Adobe PDF
208.02 kB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/713697
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 210
  • ???jsp.display-item.citation.isi??? 182
social impact