In the present work, the effect of the addition to a porcelain stoneware body of glass-ceramic frits belonging to the CaO-ZrO2-Al2O3-SiO2 (CZAS, containing 1, 3, 5, 10 mol% of Al2O3) system as replacement of the “state of art” frit belonging to CaO-ZrO2-SiO2 system (CZS) was evaluated. The firing process was performed in a furnace able to complete the thermal cycle in 50 min, in order to simulate the industrial process.Technological properties such as water absorption, firing shrinkage, flexural strength, thermal expansion behaviour were measured. Aesthetical properties were also evaluated. X-ray diffraction and scanning electron microscopy studies were also carried out to analyse the microstructure and the phase compositions of the studied samples. It was found that the sample containing the CZAS frit with 5%mol of Al2O3 shows, in general, the best combination of properties in term of mechanical, physical and aesthetical properties
Influence of CaO-ZrO2-Al2O3-SiO2 glass-ceramic frits on the technological properties of porcelain stoneware bodies / Siligardi, Cristina; Miselli, Paola; Lusvarghi, Luca; M., Reginelli. - In: CERAMICS INTERNATIONAL. - ISSN 0272-8842. - ELETTRONICO. - 37:(2011), pp. 1851-1858. [10.1016/j.ceramint.2011.03.010]
Influence of CaO-ZrO2-Al2O3-SiO2 glass-ceramic frits on the technological properties of porcelain stoneware bodies
SILIGARDI, Cristina;MISELLI, Paola;LUSVARGHI, Luca;
2011
Abstract
In the present work, the effect of the addition to a porcelain stoneware body of glass-ceramic frits belonging to the CaO-ZrO2-Al2O3-SiO2 (CZAS, containing 1, 3, 5, 10 mol% of Al2O3) system as replacement of the “state of art” frit belonging to CaO-ZrO2-SiO2 system (CZS) was evaluated. The firing process was performed in a furnace able to complete the thermal cycle in 50 min, in order to simulate the industrial process.Technological properties such as water absorption, firing shrinkage, flexural strength, thermal expansion behaviour were measured. Aesthetical properties were also evaluated. X-ray diffraction and scanning electron microscopy studies were also carried out to analyse the microstructure and the phase compositions of the studied samples. It was found that the sample containing the CZAS frit with 5%mol of Al2O3 shows, in general, the best combination of properties in term of mechanical, physical and aesthetical properties
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris