WC-CoCr coatings were HVOF-sprayed onto an AA6082T6 substrate. Thickness values between 50 and150 lm were produced by stepwise increase of the number of torch scans. This increase made thecoatings not only thicker but also denser. This was due both to peening effects and by modifications tothe splat formation mechanism, investigated by focused ion beam technique. Thanks to such densification,the hardness, the wear and impact resistance, and the corrosion protectiveness of the layersincreased with the number of torch scans. The largest improvement occurred from 2 to 3 torch scans.These coatings were also compared to anodized films: cermets had superior wear and impact resistancebut offered less corrosion protection.
Wear and Corrosion Behavior of HVOF-Sprayed WC-CoCr Coatings on Al Alloys / M., Barletta; Bolelli, Giovanni; Bonferroni, Benedetta; Lusvarghi, Luca. - In: JOURNAL OF THERMAL SPRAY TECHNOLOGY. - ISSN 1059-9630. - STAMPA. - 19:1-2(2010), pp. 358-367. [10.1007/s11666-009-9387-1]
Wear and Corrosion Behavior of HVOF-Sprayed WC-CoCr Coatings on Al Alloys
BOLELLI, Giovanni;BONFERRONI, Benedetta;LUSVARGHI, Luca
2010
Abstract
WC-CoCr coatings were HVOF-sprayed onto an AA6082T6 substrate. Thickness values between 50 and150 lm were produced by stepwise increase of the number of torch scans. This increase made thecoatings not only thicker but also denser. This was due both to peening effects and by modifications tothe splat formation mechanism, investigated by focused ion beam technique. Thanks to such densification,the hardness, the wear and impact resistance, and the corrosion protectiveness of the layersincreased with the number of torch scans. The largest improvement occurred from 2 to 3 torch scans.These coatings were also compared to anodized films: cermets had superior wear and impact resistancebut offered less corrosion protection.Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris