The thermally induced structural modifications of the natural zeolite barrerite [Na16Al16Si56O144·52H2O, a = 13.6239(4) Å, b = 18.2033(5) Å, c = 17.8317(7) Å, V = 4422.3(3) Å3, space group Amma, framework type STI] were studied in a temperature-resolved X-ray powder diffraction experiment, using synchrotron radiation, in the temperature range 339–973 K. In the initial stage of heating, up to 508 K, barrerite Phase A (space group Amma) is stable, the unit-cell volume decreases by about 4% and a water release of about 66% is observed. Between 521 and 598 K, a phase transition to the collapsed so-called barrerite Phase B (space group Amma) is observed. During the transition, the rotation of the 4254 secondary building units causes a large decrease in cell volume and deformation of the channel system. Phase B, at 611 K, shows the statistical breaking of T-O-T bridges in the 4-rings and the migration of the involved tetrahedral atoms to new “face-sharing” tetrahedra, with a consequent reduction of the free volume of the channels parallel to [100]. The new structure is stable up to 741 K and the total volume decrease is about 16%. A new phase appears from 754 K with cell parameters similar to those reported for the highly deformed barrerite Phase D and is stable up to 910 K, which is the temperature at which the total volume decrease is 22.5%. The material does not undergo amorphization up to the highest temperature investigated.
Dehydration dynamics of barrerite: An in situ synchrotron xrpd study / Ori, S.; Mazzucato, E.; Vezzalini, Maria Giovanna. - In: AMERICAN MINERALOGIST. - ISSN 0003-004X. - STAMPA. - 94:1(2009), pp. 64-73. [10.2138/am.2009.2914]
Dehydration dynamics of barrerite: An in situ synchrotron xrpd study
VEZZALINI, Maria Giovanna
2009
Abstract
The thermally induced structural modifications of the natural zeolite barrerite [Na16Al16Si56O144·52H2O, a = 13.6239(4) Å, b = 18.2033(5) Å, c = 17.8317(7) Å, V = 4422.3(3) Å3, space group Amma, framework type STI] were studied in a temperature-resolved X-ray powder diffraction experiment, using synchrotron radiation, in the temperature range 339–973 K. In the initial stage of heating, up to 508 K, barrerite Phase A (space group Amma) is stable, the unit-cell volume decreases by about 4% and a water release of about 66% is observed. Between 521 and 598 K, a phase transition to the collapsed so-called barrerite Phase B (space group Amma) is observed. During the transition, the rotation of the 4254 secondary building units causes a large decrease in cell volume and deformation of the channel system. Phase B, at 611 K, shows the statistical breaking of T-O-T bridges in the 4-rings and the migration of the involved tetrahedral atoms to new “face-sharing” tetrahedra, with a consequent reduction of the free volume of the channels parallel to [100]. The new structure is stable up to 741 K and the total volume decrease is about 16%. A new phase appears from 754 K with cell parameters similar to those reported for the highly deformed barrerite Phase D and is stable up to 910 K, which is the temperature at which the total volume decrease is 22.5%. The material does not undergo amorphization up to the highest temperature investigated.File | Dimensione | Formato | |
---|---|---|---|
Ori_p64-73_09.pdf
Accesso riservato
Tipologia:
Versione dell'autore revisionata e accettata per la pubblicazione
Dimensione
2.93 MB
Formato
Adobe PDF
|
2.93 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris