We report the results of a study on Ni-clusters assembled films deposited on Si(100) and MgO(100) surfaces. The films were produced by deposition of pre-formed Ni nanoparticles generated by a gas aggregation source. The samples topography and growth mode were investigated with SEM, AFM, STM and XPS. MOKE technique was used to determine magnetization curves at T=300 K, T=100 K and T=50K. The films show random paving growth mode, where clusters assemble in agglomerates. From MOKE data we observe a behaviour that can be ascribed to the occurrence of Super Correlated Spin Glass phase at T=300 K, and soft ferromagnetic hysteresis cycles at low temperature, possibly related with a different magnetic phase.
We report the results of a study on Ni-clusters assembled films deposited on Si(100) and MgO(100) surfaces. The films were produced by deposition of pre-formed Ni nanoparticles generated by a gas aggregation source. The samples topography and growth mode were investigated with SEM, AFM, STM and XPS. MOKE technique was used to determine magnetization curves at T=300 K, T=100 K and T=50K. The films show random paving growth mode, where clusters assemble in agglomerates. From MOKE data we observe a behaviour that can be ascribed to the occurrence of Super Correlated Spin Glass phase at T=300 K, and soft ferromagnetic hysteresis cycles at low temperature, possibly related with a different magnetic phase. © 2008 IOP Publishing Ltd.
Growth and study of Ni nanoparticles films deposited on inert subtrates / D'Addato, S.; Gragnaniello, L.; Di Bona, A.; Rota, A.; Vavassori, P.; Valeri, S.. - In: JOURNAL OF PHYSICS. CONFERENCE SERIES. - ISSN 1742-6588. - ELETTRONICO. - 100:7(2008), pp. 1-4. [10.1088/1742-6596/100/7/072046]
Growth and study of Ni nanoparticles films deposited on inert subtrates
D'addato S.;Gragnaniello L.;Di Bona A.;Rota A.;Valeri S.
2008
Abstract
We report the results of a study on Ni-clusters assembled films deposited on Si(100) and MgO(100) surfaces. The films were produced by deposition of pre-formed Ni nanoparticles generated by a gas aggregation source. The samples topography and growth mode were investigated with SEM, AFM, STM and XPS. MOKE technique was used to determine magnetization curves at T=300 K, T=100 K and T=50K. The films show random paving growth mode, where clusters assemble in agglomerates. From MOKE data we observe a behaviour that can be ascribed to the occurrence of Super Correlated Spin Glass phase at T=300 K, and soft ferromagnetic hysteresis cycles at low temperature, possibly related with a different magnetic phase. © 2008 IOP Publishing Ltd.
| File | Dimensione | Formato | |
|---|---|---|---|
|
NinanoclsJPconf.pdf
Open access
Tipologia:
VOR - Versione pubblicata dall'editore
Licenza:
[IR] closed
Dimensione
1.73 MB
Formato
Adobe PDF
|
1.73 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris