The behavior of 2 viscosity-grade polyvinyl alcohols. was studied at 2 different percentages added to the slurry used for the preparation of tableware by isostatic pressing. The modification of the porous structure, the apparent d., and the elimination of the binder were examined. Results obtained show that binders do not modify the reactions during the firing process. More evident differences are verifiable in the porosity of the green and fired bodies, according to their mol. wt. and concn. Porosity decreased until 350°C (200°C for the binder with high mol. wt.), while from 450°C (350°C high wt. binder) to 700°C it increased quickly. At higher temps., as an effect of sintering, porosity fell dramatically to <3% and residual porosity is concd. in large pores. Effect of mol. wt. is to det. a higher porosity using the binder with longer chain while the bulk d. is lower. The green body with higher percentage of adhesive presents a lower open porosity and bulk d.
Sintering and modification of porous structure caused by binders added to whiteware body composition / Andreola, Nora Maria; Romagnoli, Marcello; Pozzi, Paolo. - STAMPA. - 18 (2):(1997), pp. 12-21. (Intervento presentato al convegno 1996 98th Annual Meeting and the Ceramic Manufacturing Council's Workshop and Exposition tenutosi a Indianapolis, IN, USA nel 14 April 1996 through 17 April 1996).
Sintering and modification of porous structure caused by binders added to whiteware body composition
ANDREOLA, Nora Maria;ROMAGNOLI, Marcello;POZZI, Paolo
1997
Abstract
The behavior of 2 viscosity-grade polyvinyl alcohols. was studied at 2 different percentages added to the slurry used for the preparation of tableware by isostatic pressing. The modification of the porous structure, the apparent d., and the elimination of the binder were examined. Results obtained show that binders do not modify the reactions during the firing process. More evident differences are verifiable in the porosity of the green and fired bodies, according to their mol. wt. and concn. Porosity decreased until 350°C (200°C for the binder with high mol. wt.), while from 450°C (350°C high wt. binder) to 700°C it increased quickly. At higher temps., as an effect of sintering, porosity fell dramatically to <3% and residual porosity is concd. in large pores. Effect of mol. wt. is to det. a higher porosity using the binder with longer chain while the bulk d. is lower. The green body with higher percentage of adhesive presents a lower open porosity and bulk d.
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris