Template removal by calcination of MFI type membranes is often accompanied by crack formatìon. The thermal behavior of MFI type membranes, synthesized with and without masking, was studied to understand the mechanìsm. Masking prevents growth of zeolite in thè interior of the support during membrane synthesis. Rietveld refìnements of powder diffraction data collected in situ at high temperature allowed to accurately determine the change in thermal expansion of thè MFI film and thè porous a-alumìna support. During heating, a relatively large contraction of the celi volume during template removal occurred in thè zeolite powder and in thè film of thè membrane prepared with masking. The much smaller decrease in thè non-masked sample indicates that this membrane is under stress during heating and as a consequence, cracks are formed. The stress imposed in the membrane prepared without masking may be due to the opposite thermal behavior of the substrate in combination with strong bonds between thè membrane and thè support.

Accurate measurement of the thermal expansion of MFI zeolite membranes by in situ HTXRPD / Gualtieri, Eva Magdalena; Gualtieri, Alessandro; Hedlund, J.; Jareman, F.; Sterte, J.; Dapiaggi, M.. - STAMPA. - -:(2004), pp. 703-709. ((Intervento presentato al convegno N/A tenutosi a N/A nel N/A.

Accurate measurement of the thermal expansion of MFI zeolite membranes by in situ HTXRPD

GUALTIERI, Eva Magdalena;GUALTIERI, Alessandro;
2004

Abstract

Template removal by calcination of MFI type membranes is often accompanied by crack formatìon. The thermal behavior of MFI type membranes, synthesized with and without masking, was studied to understand the mechanìsm. Masking prevents growth of zeolite in thè interior of the support during membrane synthesis. Rietveld refìnements of powder diffraction data collected in situ at high temperature allowed to accurately determine the change in thermal expansion of thè MFI film and thè porous a-alumìna support. During heating, a relatively large contraction of the celi volume during template removal occurred in thè zeolite powder and in thè film of thè membrane prepared with masking. The much smaller decrease in thè non-masked sample indicates that this membrane is under stress during heating and as a consequence, cracks are formed. The stress imposed in the membrane prepared without masking may be due to the opposite thermal behavior of the substrate in combination with strong bonds between thè membrane and thè support.
N/A
N/A
N/A
-
703
709
Gualtieri, Eva Magdalena; Gualtieri, Alessandro; Hedlund, J.; Jareman, F.; Sterte, J.; Dapiaggi, M.
Accurate measurement of the thermal expansion of MFI zeolite membranes by in situ HTXRPD / Gualtieri, Eva Magdalena; Gualtieri, Alessandro; Hedlund, J.; Jareman, F.; Sterte, J.; Dapiaggi, M.. - STAMPA. - -:(2004), pp. 703-709. ((Intervento presentato al convegno N/A tenutosi a N/A nel N/A.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Caricamento pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11380/594231
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 7
  • ???jsp.display-item.citation.isi??? 6
social impact