In the present work, the feasibility to substitute feldspar raw material in a porcelain stoneware body with Panel Cathode Ray Tube (CRT) glasswas investigated. A standard batch and a composition, where 35 wt.% Na-feldspar was substituted by CRT glass, were sintered at differenttemperatures in the range of 1000–1250 8C. The degree of the densification was studied by evaluation of the closed and total porosity, while thesintering rate was estimated by non-isothermal dilatometric measures. The variation of the crystalline phase composition was evaluated by XRDanalysis. From the preliminary study other ceramic samples with different percentages of CRT glass (i.e. 2.5, 5 and 10 wt.%) were prepared andfired in industrial kiln. The sintering parameters, the microstructure and the mechanical properties were measured and compared with the standardcomposition.

Recycling of CRT panel glass as fluxing agent in the porcelain stoneware tile production / Andreola, Nora Maria; Barbieri, Luisa; E., Karamanova; Lancellotti, Isabella; M., Pelino. - In: CERAMICS INTERNATIONAL. - ISSN 0272-8842. - STAMPA. - 34:5(2008), pp. 1289-1295. [10.1016/j.ceramint.2007.03.013]

Recycling of CRT panel glass as fluxing agent in the porcelain stoneware tile production

ANDREOLA, Nora Maria;BARBIERI, Luisa;LANCELLOTTI, Isabella;
2008

Abstract

In the present work, the feasibility to substitute feldspar raw material in a porcelain stoneware body with Panel Cathode Ray Tube (CRT) glasswas investigated. A standard batch and a composition, where 35 wt.% Na-feldspar was substituted by CRT glass, were sintered at differenttemperatures in the range of 1000–1250 8C. The degree of the densification was studied by evaluation of the closed and total porosity, while thesintering rate was estimated by non-isothermal dilatometric measures. The variation of the crystalline phase composition was evaluated by XRDanalysis. From the preliminary study other ceramic samples with different percentages of CRT glass (i.e. 2.5, 5 and 10 wt.%) were prepared andfired in industrial kiln. The sintering parameters, the microstructure and the mechanical properties were measured and compared with the standardcomposition.
2008
34
5
1289
1295
Recycling of CRT panel glass as fluxing agent in the porcelain stoneware tile production / Andreola, Nora Maria; Barbieri, Luisa; E., Karamanova; Lancellotti, Isabella; M., Pelino. - In: CERAMICS INTERNATIONAL. - ISSN 0272-8842. - STAMPA. - 34:5(2008), pp. 1289-1295. [10.1016/j.ceramint.2007.03.013]
Andreola, Nora Maria; Barbieri, Luisa; E., Karamanova; Lancellotti, Isabella; M., Pelino
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/584755
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 101
  • ???jsp.display-item.citation.isi??? 87
social impact