EnglishMonoclinic celsian derived from an innovative route, i.e. cation exchanged zeolites heat-treated at low temperature, was added at differentcontents (10, 20, 30 wt%) to a glass matrix, in order to improve its mechanical and electrical performances. The effect of the celsian reinforcementwas evaluated by testing several properties of the composite materials, such as the elastic modulus, abrasion resistance, flexural strength andelectrical insulation. The results so far obtained suggest that the addition of the monoclinic celsian to the glass matrix may produce low-costparticulate composites with interesting technological properties.
Technological properties of celsian reinforced glass matrix composites / Cannillo, Valeria; Manfredini, Tiziano; A., Motori; F., Patuelli; A., Saccani; Sola, Antonella. - In: CERAMICS INTERNATIONAL. - ISSN 0272-8842. - STAMPA. - 33(2007), pp. 1597-1601.
| Data di pubblicazione: | 2007 | |
| Titolo: | Technological properties of celsian reinforced glass matrix composites | |
| Autore/i: | Cannillo, Valeria; Manfredini, Tiziano; A., Motori; F., Patuelli; A., Saccani; Sola, Antonella | |
| Autore/i UNIMORE: | ||
| Rivista: | ||
| Volume: | 33 | |
| Pagina iniziale: | 1597 | |
| Pagina finale: | 1601 | |
| Codice identificativo ISI: | WOS:000250424800031 | |
| Codice identificativo Scopus: | 2-s2.0-34548850309 | |
| Citazione: | Technological properties of celsian reinforced glass matrix composites / Cannillo, Valeria; Manfredini, Tiziano; A., Motori; F., Patuelli; A., Saccani; Sola, Antonella. - In: CERAMICS INTERNATIONAL. - ISSN 0272-8842. - STAMPA. - 33(2007), pp. 1597-1601. | |
| Tipologia | Articolo su rivista |
File in questo prodotto:
Pubblicazioni consigliate
http://hdl.handle.net/11380/450068
I documenti presenti in Iris Unimore sono rilasciati con licenza Creative Commons Attribuzione - Non commerciale - Non opere derivate 3.0 Italia, salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris
Copyright © 2021