Densification and microstructural changes of two glassy compositions belonging to the wollastonite and zirconia stability fields in the ternary CaO-ZrO2-SiO2 system were studied in a 2.45 GHz multimode microwave cavity. The effect of microwaves is to lower the sintering and devitrification temperature with stronger influence for high zirconia content composition. Correlation was found between dielectric properties and heating rate, showing lower interaction temperature for high zirconia content composition which starts to absorb microwave energy at about 400 degrees C compared to 800 degrees C for the low-zirconia one. Sintering and crystallization processes evolved in complex ways during heat treatment so that the two final glass-ceramic materials exhibit different microstructures, crystalline phases and mechanical properties. (C) 2000 Elsevier Science Ltd. All rights reserved.

Densification of glass powders belonging to the CaO-ZrO2-SiO2 system by microwave heating / Siligardi, Cristina; Leonelli, Cristina; F., Bondioli; Corradi, Anna; Pellacani, Gian Carlo. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - STAMPA. - 20:(2000), pp. 177-183.

Densification of glass powders belonging to the CaO-ZrO2-SiO2 system by microwave heating

SILIGARDI, Cristina;LEONELLI, Cristina;CORRADI, Anna;PELLACANI, Gian Carlo
2000

Abstract

Densification and microstructural changes of two glassy compositions belonging to the wollastonite and zirconia stability fields in the ternary CaO-ZrO2-SiO2 system were studied in a 2.45 GHz multimode microwave cavity. The effect of microwaves is to lower the sintering and devitrification temperature with stronger influence for high zirconia content composition. Correlation was found between dielectric properties and heating rate, showing lower interaction temperature for high zirconia content composition which starts to absorb microwave energy at about 400 degrees C compared to 800 degrees C for the low-zirconia one. Sintering and crystallization processes evolved in complex ways during heat treatment so that the two final glass-ceramic materials exhibit different microstructures, crystalline phases and mechanical properties. (C) 2000 Elsevier Science Ltd. All rights reserved.
20
177
183
Densification of glass powders belonging to the CaO-ZrO2-SiO2 system by microwave heating / Siligardi, Cristina; Leonelli, Cristina; F., Bondioli; Corradi, Anna; Pellacani, Gian Carlo. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - STAMPA. - 20:(2000), pp. 177-183.
Siligardi, Cristina; Leonelli, Cristina; F., Bondioli; Corradi, Anna; Pellacani, Gian Carlo
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Caricamento pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11380/310756
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 41
  • ???jsp.display-item.citation.isi??? 36
social impact