EnglishRecently, the traditional ceramic industry has demonstrated increased interest in obtaining inclusion pigments to stabilize unstable chromophores, such as hematite or cadmium sulfoselenide, at firing temperature and in studying the actions of molten glasses. This present work focuses on a new method for synthesizing hematite-zircon inclusion pigments from an unconventional mixture of precursors. For this purpose, a glassy composition that belongs to the LiO2-ZrO2-SiO2 system and that crystallizes into zircon during the calcination step has been chosen.
New glass-ceramic inclusion pigment / F., Bondioli; Manfredini, Tiziano; Siligardi, Cristina; Ferrari, Anna Maria. - In: JOURNAL OF THE AMERICAN CERAMIC SOCIETY. - ISSN 0002-7820. - STAMPA. - 88(2005), pp. 1070-1071.
| Data di pubblicazione: | 2005 | |
| Titolo: | New glass-ceramic inclusion pigment | |
| Autore/i: | F., Bondioli; Manfredini, Tiziano; Siligardi, Cristina; Ferrari, Anna Maria | |
| Autore/i UNIMORE: | ||
| Rivista: | ||
| Volume: | 88 | |
| Pagina iniziale: | 1070 | |
| Pagina finale: | 1071 | |
| Codice identificativo ISI: | WOS:000228354900059 | |
| Codice identificativo Scopus: | 2-s2.0-27644469438 | |
| Citazione: | New glass-ceramic inclusion pigment / F., Bondioli; Manfredini, Tiziano; Siligardi, Cristina; Ferrari, Anna Maria. - In: JOURNAL OF THE AMERICAN CERAMIC SOCIETY. - ISSN 0002-7820. - STAMPA. - 88(2005), pp. 1070-1071. | |
| Tipologia | Articolo su rivista |
File in questo prodotto:
Pubblicazioni consigliate
http://hdl.handle.net/11380/310720
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris
Copyright © 2021