Reutilization of waste inert glass from the disposal of polluted dredging spoils by the obtainment of ceramic products for tiles applications

The vitrification treatment has been successfully exploited as a solution for the disposal of polluted dredging spoils from the industrial area close to the Venice Lagoon. The addition of 20% by wt. of glass cullet to the calcined sediments in the vitrification batch provides a suitable chemical composition for the production of an inert glass, despite the compositional variations of the sediments. The obtained waste glass, after being finely ground, has been employed (i) as a raw material for the manufacture of sintered glass-ceramics, by cold pressing and single-step sintering at about 940 degrees C, and (ii) as sintering additive (the maximum addition being 10% by wt.) for the manufacture of traditional red single firing ceramic tiles, with a maximum firing temperature of 1186 degrees C. Both applications have proved to be promising: in the first case, the sintered glass ceramic product exhibits notable mechanical properties (bending strength > 130 MPa, HV approximate to 6.5 GPa); in the second case, the addition of waste glass does not modify substantially the investigated physical and mechanical properties of the traditional product (water absorption, linear shrinkage, bending strength, planarity).