The synthesis and the structural, thermal, and electrical characterization of haloplumbate(II) systems are described. The counterions are diprotonated Linear aliphatic amines, such as the 2-methylpentane-1,5-diamine (2meptH(2)) and propane-1,3-diamine (pnH(2)) dications. The (2meptH(2))[PbCl4] and (2meptH(2))[PbBr4] are isostructural, space group Cc, with a = 24.140(4) Angstrom, b = 7.720(2) Angstrom, c = 7.795(2) Angstrom, beta = 98.1(1)degrees, Z = 4 for the chlorine compound and a = 24.539(4) Angstrom, b = 8.031(2) Angstrom, c = 8.198(2) Angstrom, beta = 99.6(1)degrees, Z = 4 for the bromine compound; the (2meptH(2))[Pb1.5I5] crystallizes in the triclinic P (1) over bar space group, with a = 11.803(3) Angstrom, b = 12.565(3) Angstrom, c = 8.494(8) Angstrom, alpha = 106.2(1)degrees, beta = 100.5(1)degrees, gamma = 117.4(1)degrees, Z = 2; the crystals of (pnH(2))[PbCl4] are orthorhombic, space group P2(1)2(1)2(1), a = 19.247(4) Angstrom, b = 7.862(2) Angstrom, c = 7.581(2) Angstrom, Z = 4; the (pnH(2))(2)[Pb1.5Br7]. H2O crystallizes in the triclinic P (1) over bar space group, with a = 11.517(3) Angstrom, b = 14.122(3) Angstrom, c = 8.149(2) Angstrom, alpha = 104.1(1)degrees, beta = 109.8(1)degrees, gamma = 77.5(1)degrees, Z = 2. Three different types of polymeric haloplumbate(II) systems were obtained: strictly monodimensional, (2meptH(2))[Pb1.5I5], ribbonlike, (pnH(2))(2)[Pb1.5Br7]. H2O, and perovskite-like structures, (pnH(2))[PbCl4] and (2meptH(2))[PbX4] (X = Cl, Br). Worthy of note is the presence of organic dications in their extended form, intercalated between the inorganic anions, which are at different distances, depending on the amine length. The nitrogen atoms of the ammonium cations interact with the inorganic anions forming a network of hydrogen bonds, which contribute to the crystal packing.

Structural and electrical characterization of polymeric haloplumbate(II) systems / Corradi, Anna; Ferrari, Anna Maria; Pellacani, Gian Carlo; A., Saccani; F., Sandrolini; P., Sgarabotto. - In: INORGANIC CHEMISTRY. - ISSN 0020-1669. - STAMPA. - 38 (4):(1999), pp. 716-721.

Structural and electrical characterization of polymeric haloplumbate(II) systems

CORRADI, Anna;FERRARI, Anna Maria;PELLACANI, Gian Carlo;
1999

Abstract

The synthesis and the structural, thermal, and electrical characterization of haloplumbate(II) systems are described. The counterions are diprotonated Linear aliphatic amines, such as the 2-methylpentane-1,5-diamine (2meptH(2)) and propane-1,3-diamine (pnH(2)) dications. The (2meptH(2))[PbCl4] and (2meptH(2))[PbBr4] are isostructural, space group Cc, with a = 24.140(4) Angstrom, b = 7.720(2) Angstrom, c = 7.795(2) Angstrom, beta = 98.1(1)degrees, Z = 4 for the chlorine compound and a = 24.539(4) Angstrom, b = 8.031(2) Angstrom, c = 8.198(2) Angstrom, beta = 99.6(1)degrees, Z = 4 for the bromine compound; the (2meptH(2))[Pb1.5I5] crystallizes in the triclinic P (1) over bar space group, with a = 11.803(3) Angstrom, b = 12.565(3) Angstrom, c = 8.494(8) Angstrom, alpha = 106.2(1)degrees, beta = 100.5(1)degrees, gamma = 117.4(1)degrees, Z = 2; the crystals of (pnH(2))[PbCl4] are orthorhombic, space group P2(1)2(1)2(1), a = 19.247(4) Angstrom, b = 7.862(2) Angstrom, c = 7.581(2) Angstrom, Z = 4; the (pnH(2))(2)[Pb1.5Br7]. H2O crystallizes in the triclinic P (1) over bar space group, with a = 11.517(3) Angstrom, b = 14.122(3) Angstrom, c = 8.149(2) Angstrom, alpha = 104.1(1)degrees, beta = 109.8(1)degrees, gamma = 77.5(1)degrees, Z = 2. Three different types of polymeric haloplumbate(II) systems were obtained: strictly monodimensional, (2meptH(2))[Pb1.5I5], ribbonlike, (pnH(2))(2)[Pb1.5Br7]. H2O, and perovskite-like structures, (pnH(2))[PbCl4] and (2meptH(2))[PbX4] (X = Cl, Br). Worthy of note is the presence of organic dications in their extended form, intercalated between the inorganic anions, which are at different distances, depending on the amine length. The nitrogen atoms of the ammonium cations interact with the inorganic anions forming a network of hydrogen bonds, which contribute to the crystal packing.
1999
38 (4)
716
721
Structural and electrical characterization of polymeric haloplumbate(II) systems / Corradi, Anna; Ferrari, Anna Maria; Pellacani, Gian Carlo; A., Saccani; F., Sandrolini; P., Sgarabotto. - In: INORGANIC CHEMISTRY. - ISSN 0020-1669. - STAMPA. - 38 (4):(1999), pp. 716-721.
Corradi, Anna; Ferrari, Anna Maria; Pellacani, Gian Carlo; A., Saccani; F., Sandrolini; P., Sgarabotto
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/307809
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 58
  • ???jsp.display-item.citation.isi??? 56
social impact