Basic principles of fabricating tile glazes based on cordieritic glass-ceramics are explained. Glass compositions from the MgO-Al2O3SiO2 three-component phase diagram have been melted with and without the nucleating agent TiO2. Additionally, a sodium borosilicate glass that is commonly used in the the glaze industry has been wet milled, together with the previous compositions, to produce a coating slip. Studies are focused on the role of the nucleating agent and glassy formulation in the crystallization of the glass-ceramic system using differential thermal analysis, X-ray diffractometry, and scanning electron microscopy. When added to a borosilicate glass, only one composition is capable of crystallizing cordierite under a fast-firing cycle used for ''monoporosa'' production. The porosity of the glaze layer is sufficiently low and the crystal size is small to ensure good mechanical and chemical properties, The presence of cordierite crystals in the glaze should enhance abrasion and acid resistance, in comparison to a traditional matte glaze that contains mostly enstatite or diopside crystals.
Feasibility of using cordierite class-ceramics as tile glazes / Ferrari, Anna Maria; Barbieri, Luisa; Leonelli, Cristina; Manfredini, Tiziano; Siligardi, Cristina; Corradi, Anna. - In: JOURNAL OF THE AMERICAN CERAMIC SOCIETY. - ISSN 0002-7820. - STAMPA. - 80(7):(1997), pp. 1757-1766.
Feasibility of using cordierite class-ceramics as tile glazes
FERRARI, Anna Maria;BARBIERI, Luisa;LEONELLI, Cristina;MANFREDINI, Tiziano;SILIGARDI, Cristina;CORRADI, Anna
1997
Abstract
Basic principles of fabricating tile glazes based on cordieritic glass-ceramics are explained. Glass compositions from the MgO-Al2O3SiO2 three-component phase diagram have been melted with and without the nucleating agent TiO2. Additionally, a sodium borosilicate glass that is commonly used in the the glaze industry has been wet milled, together with the previous compositions, to produce a coating slip. Studies are focused on the role of the nucleating agent and glassy formulation in the crystallization of the glass-ceramic system using differential thermal analysis, X-ray diffractometry, and scanning electron microscopy. When added to a borosilicate glass, only one composition is capable of crystallizing cordierite under a fast-firing cycle used for ''monoporosa'' production. The porosity of the glaze layer is sufficiently low and the crystal size is small to ensure good mechanical and chemical properties, The presence of cordierite crystals in the glaze should enhance abrasion and acid resistance, in comparison to a traditional matte glaze that contains mostly enstatite or diopside crystals.Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris