Poly(epsilon-caprolactone-b-perfluoropolyether-b-epsilon caprolactone) (PCL-PFPE-PCL) block copolymers having different PCL block lengths and end-capped with methacrylate groups were prepared and characterized. Spectroscopic analyses confirmed the expected molecular structure of the products. After UV curing, the films revealed the presence of two amorphous phases, corresponding to fluorinated and hydrogenated moieties, respectively. The material containing long PCL blocks showed also a crystalline phase. Surface properties of the UV-cured films were evaluated: The surfaces have a very high hydrophobic character in spite of the presence of many polar OH groups present in the polymeric network and a high hysteresis in wetting. An enrichment of fluorine at the air-side surface was shown by contact-angle measurements, except when long PCL sequences are present. The theta(adv) angles decreased by increasing the content of PCL, that is, by decreasing the content of fluorine.
Acrylic polyester resins containing perfluoropolyethers structures: Synthesis, characterization, and photopolymerization / R., Bongiovanni; G., Malucelli; Messori, Massimo; Pilati, Francesco; A., Priola; C., Tonelli; M., Toselli. - In: JOURNAL OF APPLIED POLYMER SCIENCE. - ISSN 0021-8995. - STAMPA. - 75:5(2000), pp. 651-659. [10.1002/(SICI)1097-4628(20000131)75:5<651::AID-APP7>3.0.CO;2-P]
Acrylic polyester resins containing perfluoropolyethers structures: Synthesis, characterization, and photopolymerization
MESSORI, Massimo;PILATI, Francesco;
2000
Abstract
Poly(epsilon-caprolactone-b-perfluoropolyether-b-epsilon caprolactone) (PCL-PFPE-PCL) block copolymers having different PCL block lengths and end-capped with methacrylate groups were prepared and characterized. Spectroscopic analyses confirmed the expected molecular structure of the products. After UV curing, the films revealed the presence of two amorphous phases, corresponding to fluorinated and hydrogenated moieties, respectively. The material containing long PCL blocks showed also a crystalline phase. Surface properties of the UV-cured films were evaluated: The surfaces have a very high hydrophobic character in spite of the presence of many polar OH groups present in the polymeric network and a high hysteresis in wetting. An enrichment of fluorine at the air-side surface was shown by contact-angle measurements, except when long PCL sequences are present. The theta(adv) angles decreased by increasing the content of PCL, that is, by decreasing the content of fluorine.Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris