Structural and colour changes induced by increasing amounts of vanadium oxide. V2O5, are presented for a near formulation of glass with composition 37CaO, 6ZrO(2), 57SiO(2) (mol%). Property changes were evaluated by measuring density, chemical durability and microhardness of glasses with increasing amount of vanadium oxide. Vanadium oxide imparts to tire glass a light green colour, not dissimilar to that from chromium, at low content, while at higher concentration the colour changes to dark brown. Spectroscopic technique, VIS-NIR and ESR were rued to identify tire chromophore centres in terms of vanadium oxidation state and coordination which there subsequently correlated to property changes. Experimental evidence is reported for an equilibrium between two species. V5+-tetrahedral and V4+ tetragonally distorted octahedral.
Vanadium doping in CaO-ZrO2-SiO2 glasses / Siligardi, Cristina; Ferrari, Anna Maria; Leonelli, Cristina; S., Bruni. - In: PHYSICS AND CHEMISTRY OF GLASSES. - ISSN 0031-9090. - STAMPA. - 43:2(2002), pp. 97-101.
Vanadium doping in CaO-ZrO2-SiO2 glasses
SILIGARDI, Cristina;FERRARI, Anna Maria;LEONELLI, Cristina;
2002
Abstract
Structural and colour changes induced by increasing amounts of vanadium oxide. V2O5, are presented for a near formulation of glass with composition 37CaO, 6ZrO(2), 57SiO(2) (mol%). Property changes were evaluated by measuring density, chemical durability and microhardness of glasses with increasing amount of vanadium oxide. Vanadium oxide imparts to tire glass a light green colour, not dissimilar to that from chromium, at low content, while at higher concentration the colour changes to dark brown. Spectroscopic technique, VIS-NIR and ESR were rued to identify tire chromophore centres in terms of vanadium oxidation state and coordination which there subsequently correlated to property changes. Experimental evidence is reported for an equilibrium between two species. V5+-tetrahedral and V4+ tetragonally distorted octahedral.
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris