Objectives: The aim of this study is to determine the cyclic fatigue resistance of Mtwo Minimal in static and dynamic tests, with different amplitudes of pecking movements, at intracanal temperature.Materials and Methods: Two hundred new 25-mm Mtwo Minimal rotary files (#10/0.035, #17.5/0.045, #25/0.05, #40/0.03, #45/0.03) were tested in static and dynamic cyclic fatigue tests at 35 degrees C (+/- 1 degrees C). An artificial stainless-steel canal was used. In the dynamic mode, axial movements were set at 1 and 3 mm. The number of cycles to fracture (NCF) was recorded and statistically analyzed by one-way analysis of variance (p < 0.05).Results: The 3-mm dynamic test showed significantly increased NCF than the other tests for the #10/0.035, #17.5/0.045, and #25/0.05 files (p < 0.05). The #40/0.03 and #45/0.03 files showed no significant differences in all the tests (p > 0.05).Conclusion: Mtwo Minimal showed higher cyclic fatigue resistance in the dynamic test than the static test, except for the larger instruments. The 3-mm pecking amplitude increased the cyclic fatigue resistance of the smaller instruments.
Impact of pecking amplitude on cyclic fatigue of new nickel–titanium files / Pedullà, E.; Carlesi, T.; Pappalardo, A.; Canova, F. S.; Malagnino, V. A.; La Rosa, G. R. M.; Generali, L.. - In: CLINICAL AND EXPERIMENTAL DENTAL RESEARCH. - ISSN 2057-4347. - 10:1(2024), pp. 1-7. [10.1002/cre2.811]
Impact of pecking amplitude on cyclic fatigue of new nickel–titanium files
Generali L.
2024
Abstract
Objectives: The aim of this study is to determine the cyclic fatigue resistance of Mtwo Minimal in static and dynamic tests, with different amplitudes of pecking movements, at intracanal temperature.Materials and Methods: Two hundred new 25-mm Mtwo Minimal rotary files (#10/0.035, #17.5/0.045, #25/0.05, #40/0.03, #45/0.03) were tested in static and dynamic cyclic fatigue tests at 35 degrees C (+/- 1 degrees C). An artificial stainless-steel canal was used. In the dynamic mode, axial movements were set at 1 and 3 mm. The number of cycles to fracture (NCF) was recorded and statistically analyzed by one-way analysis of variance (p < 0.05).Results: The 3-mm dynamic test showed significantly increased NCF than the other tests for the #10/0.035, #17.5/0.045, and #25/0.05 files (p < 0.05). The #40/0.03 and #45/0.03 files showed no significant differences in all the tests (p > 0.05).Conclusion: Mtwo Minimal showed higher cyclic fatigue resistance in the dynamic test than the static test, except for the larger instruments. The 3-mm pecking amplitude increased the cyclic fatigue resistance of the smaller instruments.File | Dimensione | Formato | |
---|---|---|---|
IMPACT OF PECKING AMPLITUDE.pdf
Open access
Tipologia:
VOR - Versione pubblicata dall'editore
Dimensione
1.56 MB
Formato
Adobe PDF
|
1.56 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris