: Geopolymers are amorphous aluminosilicate inorganic polymers synthesized by alkaline activation characterized by a lower carbon footprint, greater durability, and excellent mechanical properties compared to traditional concrete, making them promising building materials for sustainable construction. To develop sustainable lightweight geopolymer-based building materials useful as fire resistant thermal insulation materials, we added 5 and 10 wt% of discarded cork dust, a readily available industrial by-product, to metakaolin before and after the alkaline activation with sodium hydroxide 8 M and sodium silicate solutions. We followed the chemical, microstructural, antibacterial, and physical properties of the resulting composites for up to 90 days in order to monitor their long-term durability. The presence of cork does not interfere with the geopolymerization process and in fact reduces the density of the composites to values around 2.5 g/cm3, especially when added after alkaline activation. The composites resulted in chemically stable matrices (less than 10 ppm of cations release) and filler (no hazardous compounds released) with a bacterial viability of around 80%. This study provides valuable insights into the tailoring of discarded cork-based composites obtained by geopolymerization with a porosity between 32 and 48% and a mechanical resistance to compression from 15 to 5 MPa, respectively, suggesting their potential as durable interior panels with low environmental impact and desirable performance.
Long-term durability of discarded cork-based composites obtained by geopolymerization / Poggetto, G. D.; Barbieri, L.; D'Angelo, A.; Zambon, A.; Zardi, P.; Leonelli, C.. - In: ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH INTERNATIONAL. - ISSN 0944-1344. - (2024), pp. ---. [10.1007/s11356-024-33958-8]
Long-term durability of discarded cork-based composites obtained by geopolymerization
Barbieri L.
;Zambon A.;Zardi P.;Leonelli C.
2024
Abstract
: Geopolymers are amorphous aluminosilicate inorganic polymers synthesized by alkaline activation characterized by a lower carbon footprint, greater durability, and excellent mechanical properties compared to traditional concrete, making them promising building materials for sustainable construction. To develop sustainable lightweight geopolymer-based building materials useful as fire resistant thermal insulation materials, we added 5 and 10 wt% of discarded cork dust, a readily available industrial by-product, to metakaolin before and after the alkaline activation with sodium hydroxide 8 M and sodium silicate solutions. We followed the chemical, microstructural, antibacterial, and physical properties of the resulting composites for up to 90 days in order to monitor their long-term durability. The presence of cork does not interfere with the geopolymerization process and in fact reduces the density of the composites to values around 2.5 g/cm3, especially when added after alkaline activation. The composites resulted in chemically stable matrices (less than 10 ppm of cations release) and filler (no hazardous compounds released) with a bacterial viability of around 80%. This study provides valuable insights into the tailoring of discarded cork-based composites obtained by geopolymerization with a porosity between 32 and 48% and a mechanical resistance to compression from 15 to 5 MPa, respectively, suggesting their potential as durable interior panels with low environmental impact and desirable performance.File | Dimensione | Formato | |
---|---|---|---|
s11356-024-33958-8_paper published.pdf
Accesso riservato
Tipologia:
Versione pubblicata dall'editore
Dimensione
2.31 MB
Formato
Adobe PDF
|
2.31 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris