Different chemical and physical treatments have been used to improve the properties and functionalities of steels. Anodizing is one of the most promising treatments, due to its versatility and easy industrial implementation. It allows the growth of nanoestructured oxide films with interesting properties able to be employed in different industrial sectors. The present work studies the influence of the anodizing time (15, 30, 45 and 60 min), as well as the stirring speed (0, 200, 400, and 600 rpm), on the morphology and the corrosion resistance of the anodic layers grown in 304L stainless steel. The anodic layers were characterized morphologically, compositionally, and electrochemically, in order to determine the influence of the anodization parameters on their corrosion behavior in a 0.6 mol L-1 NaCl solution. The results show that at 45 and 60 min anodizing times, the formation of two microstructures is favored, associated with the collapse of the nanoporous structures at the metal-oxide interphace. However, both the stirring speed and the anodizing time have a negligeable effect on the corrosion behavior of the anodized 304L SS samples, since their electrochemical values are similar to those of the non-anodized ones.

Corrosion resistance of anodic layers grown on 304L stainless steel at different anodizing times and stirring speeds / Dominguez-Jaimes, L. P.; Vara, M. AA.; Cedillo-Gonzalez, E. I.; Valdes, J. J. R.; De Damborenea, J. J.; Del Campo, A. C.; Rodriguez-Varela, F. J.; Alonso-Lemus, I. L.; Hernandez-Lopez, J. M.. - In: COATINGS. - ISSN 2079-6412. - 9:11(2019), pp. 706-706. [10.3390/coatings9110706]

Corrosion resistance of anodic layers grown on 304L stainless steel at different anodizing times and stirring speeds

Cedillo-Gonzalez E. I.
Writing – Review & Editing
;
2019

Abstract

Different chemical and physical treatments have been used to improve the properties and functionalities of steels. Anodizing is one of the most promising treatments, due to its versatility and easy industrial implementation. It allows the growth of nanoestructured oxide films with interesting properties able to be employed in different industrial sectors. The present work studies the influence of the anodizing time (15, 30, 45 and 60 min), as well as the stirring speed (0, 200, 400, and 600 rpm), on the morphology and the corrosion resistance of the anodic layers grown in 304L stainless steel. The anodic layers were characterized morphologically, compositionally, and electrochemically, in order to determine the influence of the anodization parameters on their corrosion behavior in a 0.6 mol L-1 NaCl solution. The results show that at 45 and 60 min anodizing times, the formation of two microstructures is favored, associated with the collapse of the nanoporous structures at the metal-oxide interphace. However, both the stirring speed and the anodizing time have a negligeable effect on the corrosion behavior of the anodized 304L SS samples, since their electrochemical values are similar to those of the non-anodized ones.
2019
ott-2019
9
11
706
706
Corrosion resistance of anodic layers grown on 304L stainless steel at different anodizing times and stirring speeds / Dominguez-Jaimes, L. P.; Vara, M. AA.; Cedillo-Gonzalez, E. I.; Valdes, J. J. R.; De Damborenea, J. J.; Del Campo, A. C.; Rodriguez-Varela, F. J.; Alonso-Lemus, I. L.; Hernandez-Lopez, J. M.. - In: COATINGS. - ISSN 2079-6412. - 9:11(2019), pp. 706-706. [10.3390/coatings9110706]
Dominguez-Jaimes, L. P.; Vara, M. AA.; Cedillo-Gonzalez, E. I.; Valdes, J. J. R.; De Damborenea, J. J.; Del Campo, A. C.; Rodriguez-Varela, F. J.; Alonso-Lemus, I. L.; Hernandez-Lopez, J. M.
File in questo prodotto:
File Dimensione Formato  
Dominguez-Jaimes et al, Coatings 9 (2019) 706.pdf

Open access

Descrizione: Dominguez-Jaimes et al, Coatings 9 (2019) 706
Tipologia: Versione pubblicata dall'editore
Dimensione 4.16 MB
Formato Adobe PDF
4.16 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1289649
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 15
  • ???jsp.display-item.citation.isi??? 14
social impact