Purpose: To compare the shear bond strengths (SBS) of two cements to two Y-TZP ceramics subjected to different surface treatments. Materials and Methods: Zirconia specimens were made from Lava (n = 36) and IPS e.max ZirCAD (n = 36), and their surfaces were treated as follows: no treatment (control), silica coating with 30-µm silica-modified alumina (Al2O3) particles (CoJet Sand), or coating with liners Lava Ceram for Lava and Intensive ZirLiner for IPS e.max ZirCAD. Composite resin cylinders were bonded to zirconia with Panavia F or RelyX Unicem resin cements. All specimens were thermocycled (6000 cycles at 5°C/55°C) and subjected to SBS testing. Data were analyzed by three-way ANOVA and Tukey's (HSD) post-hoc test (α = 0.05). Failure mode was analyzed by stereomicroscope and SEM. Results: CoJet Sand and liners promoted significantly higher SBS than their control groups, but had similar results to one another. Panavia F provided significantly higher SBS values than RelyX Unicem (p < 0.01) for nontreated zirconia specimens of both brands. When Lava and IPS e.max ZirCAD were abraded with CoJet Sand, RelyX Unicem promoted significantly higher SBS values than Panavia F (p < 0.001). There was no significant difference between the two cements when the zirconia specimens were treated with their respective liners. The nontreated specimens and those treated with CoJet Sand exhibited a high percentage of adhesive and mixed A failures, while the specimens treated with liners presented an increase in mixed A and mixed C failures as well as some cohesive failure in the bulk of Lava Ceram for both cements. Conclusion: CoJet Sand and liners provided the best surface treatment for Lava and IPS e.max ZirCAD. The best surface treatment/cement combinations were CoJet Sand/RelyX Unicem and liner/Panavia F. SBS of Panavia F and RelyX Unicem was not influenced by the zirconia brand.
Efficacy of surface treatments on the bond strength of resin cements to two brands of zirconia ceramic / Baldissara, P; Querzè, M; Monaco, C; Scotti, R; Fonseca, Rg.. - In: JOURNAL OF ADHESIVE DENTISTRY. - ISSN 1461-5185. - 15:4(2013), pp. 259-267. [10.3290/j.jad.a28729]
Efficacy of surface treatments on the bond strength of resin cements to two brands of zirconia ceramic
Monaco C;
2013
Abstract
Purpose: To compare the shear bond strengths (SBS) of two cements to two Y-TZP ceramics subjected to different surface treatments. Materials and Methods: Zirconia specimens were made from Lava (n = 36) and IPS e.max ZirCAD (n = 36), and their surfaces were treated as follows: no treatment (control), silica coating with 30-µm silica-modified alumina (Al2O3) particles (CoJet Sand), or coating with liners Lava Ceram for Lava and Intensive ZirLiner for IPS e.max ZirCAD. Composite resin cylinders were bonded to zirconia with Panavia F or RelyX Unicem resin cements. All specimens were thermocycled (6000 cycles at 5°C/55°C) and subjected to SBS testing. Data were analyzed by three-way ANOVA and Tukey's (HSD) post-hoc test (α = 0.05). Failure mode was analyzed by stereomicroscope and SEM. Results: CoJet Sand and liners promoted significantly higher SBS than their control groups, but had similar results to one another. Panavia F provided significantly higher SBS values than RelyX Unicem (p < 0.01) for nontreated zirconia specimens of both brands. When Lava and IPS e.max ZirCAD were abraded with CoJet Sand, RelyX Unicem promoted significantly higher SBS values than Panavia F (p < 0.001). There was no significant difference between the two cements when the zirconia specimens were treated with their respective liners. The nontreated specimens and those treated with CoJet Sand exhibited a high percentage of adhesive and mixed A failures, while the specimens treated with liners presented an increase in mixed A and mixed C failures as well as some cohesive failure in the bulk of Lava Ceram for both cements. Conclusion: CoJet Sand and liners provided the best surface treatment for Lava and IPS e.max ZirCAD. The best surface treatment/cement combinations were CoJet Sand/RelyX Unicem and liner/Panavia F. SBS of Panavia F and RelyX Unicem was not influenced by the zirconia brand.Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris