YSZ was added to glass frit in order to improve properties of the glass-ceramic dental materials by casting into a graphite mold and a cast iron mold and then crystallized via heat treatment. XRD results presented the similar crystalline phases of phlogopite-calcium mica and tetragonal zirconia in both molds. Microstructures by SEM showed the different crystal morphology due to casting molds. The slow cooling of graphite mold produced the equiaxed crystals whereas the fast cooling of cast iron mold promoted rod-like, and YSZ addition increased the number of crystals. The properties depended on the crystal morphology and crystallinity. The 5 wt% YSZ added glass-ceramic from graphite mold developed the equiaxed crystals to present the desirable properties of 147.15 MPa, flexural strength, 251.80 µg/cm2, chemical solubility and 9.26 × 10-6/°C CTE. The results were accepted by ISO 6872:2015 (Dentistry-Ceramic Materials) in type II class 2b as a partially and fully covered single substructure and matched with commercial porcelains.

Relating type of mold materials to crystal morphology and properties of glass-ceramics with YSZ additions as a dental material / Angkulpipat, S.; Srichumpong, T.; Prasertwong, S.; Meechoowas, E.; Sirinukunwattana, K.; Heness, G.; Rosa, R.; Suputtamongkol, K.; Chaysuwan, D.. - In: WARASAN KHANA WITTHAYASAT MAHA WITTHAYALAI CHIANG MAI. - ISSN 0125-2526. - 47:6(2020), pp. 1283-1296.

Relating type of mold materials to crystal morphology and properties of glass-ceramics with YSZ additions as a dental material

Rosa R.;
2020

Abstract

YSZ was added to glass frit in order to improve properties of the glass-ceramic dental materials by casting into a graphite mold and a cast iron mold and then crystallized via heat treatment. XRD results presented the similar crystalline phases of phlogopite-calcium mica and tetragonal zirconia in both molds. Microstructures by SEM showed the different crystal morphology due to casting molds. The slow cooling of graphite mold produced the equiaxed crystals whereas the fast cooling of cast iron mold promoted rod-like, and YSZ addition increased the number of crystals. The properties depended on the crystal morphology and crystallinity. The 5 wt% YSZ added glass-ceramic from graphite mold developed the equiaxed crystals to present the desirable properties of 147.15 MPa, flexural strength, 251.80 µg/cm2, chemical solubility and 9.26 × 10-6/°C CTE. The results were accepted by ISO 6872:2015 (Dentistry-Ceramic Materials) in type II class 2b as a partially and fully covered single substructure and matched with commercial porcelains.
2020
47
6
1283
1296
Relating type of mold materials to crystal morphology and properties of glass-ceramics with YSZ additions as a dental material / Angkulpipat, S.; Srichumpong, T.; Prasertwong, S.; Meechoowas, E.; Sirinukunwattana, K.; Heness, G.; Rosa, R.; Suputtamongkol, K.; Chaysuwan, D.. - In: WARASAN KHANA WITTHAYASAT MAHA WITTHAYALAI CHIANG MAI. - ISSN 0125-2526. - 47:6(2020), pp. 1283-1296.
Angkulpipat, S.; Srichumpong, T.; Prasertwong, S.; Meechoowas, E.; Sirinukunwattana, K.; Heness, G.; Rosa, R.; Suputtamongkol, K.; Chaysuwan, D....espandi
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1226855
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 1
  • ???jsp.display-item.citation.isi??? 1
social impact