Valorization of Al slag in the production of green ceramic tiles: Effect of experimental conditions on microstructure and crystalline phase composition

This work reports the results of an investigation aimed at the development of sintered glass-ceramic tiles by the sinter-crystallization of mixtures composed of aluminum slag and reclaimed packaging glass. The thermal behaviors of mixtures incorporating 50 and 60 wt% Al slag were established by differential thermal analysis (DTA). Green compacts were sintered in a temperature range of 800°C-1050°C and then soaked for 10-60 minutes. The mineralogical characterizations of the sintered materials were obtained by X-ray diffraction (XRD). The achieved results indicated that the sintering of aluminum slag and packaging glass reclaimed led to a glass-ceramic material composed mainly of needle-like crystals of wollastonite (CaSiO3). The bloating of samples during firing was evaluated according to a Cougny predictive diagram. After initial observations and according to bending strength characterizations, sintered tiles prepared from aluminum slag and glassy sand are appropriate for floor pavement and wall covering.