This study is focused on the synthesis of zirconia nanopowders stabilized by 6%mol calcia prepared under hydrothermal conditions using microwave technology. Sodium hydroxide-based hydrolysis of zirconyl chloride solution containing calcium nitrate followed by microwave irradiation at the temperature of 220 °C for 30 min was sufficient to obtain white powders of crystalline calcia stabilized zirconia. By means of X-ray diffraction and transmission electron microscopy, it was shown that tetragonal zirconia nanocrystallites with a size of ca 7 nm and diameter/standard deviation ratio of 0.10 were formed. The effects of the [Ca2+] and [NaOH] as well as temperature and time of microwave irradiation on the density and specific surface area were evaluated. Sintering test of the tetragonal nanopowders at 1,300 °C in air was performed in a monomode microwave applicator. The sample was sintered to the density of 95% and the grain size, analyzed by field emission scanning electron microscopy, was in the range from 90 to 170 nm. © 2009 Springer Science+Business Media B.V.

Microwave technique applied to the hydrothermal synthesis and sintering of calcia stabilized zirconia nanoparticles / Rizzuti, A.; Corradi, A.; Leonelli, C.; Rosa, R.; Pielaszek, R.; Lojkowski, W.. - In: JOURNAL OF NANOPARTICLE RESEARCH. - ISSN 1388-0764. - 12:1(2010), pp. 327-335. [10.1007/s11051-009-9619-9]

Microwave technique applied to the hydrothermal synthesis and sintering of calcia stabilized zirconia nanoparticles

Rizzuti A.;Corradi A.;Leonelli C.;Rosa R.;
2010

Abstract

This study is focused on the synthesis of zirconia nanopowders stabilized by 6%mol calcia prepared under hydrothermal conditions using microwave technology. Sodium hydroxide-based hydrolysis of zirconyl chloride solution containing calcium nitrate followed by microwave irradiation at the temperature of 220 °C for 30 min was sufficient to obtain white powders of crystalline calcia stabilized zirconia. By means of X-ray diffraction and transmission electron microscopy, it was shown that tetragonal zirconia nanocrystallites with a size of ca 7 nm and diameter/standard deviation ratio of 0.10 were formed. The effects of the [Ca2+] and [NaOH] as well as temperature and time of microwave irradiation on the density and specific surface area were evaluated. Sintering test of the tetragonal nanopowders at 1,300 °C in air was performed in a monomode microwave applicator. The sample was sintered to the density of 95% and the grain size, analyzed by field emission scanning electron microscopy, was in the range from 90 to 170 nm. © 2009 Springer Science+Business Media B.V.
2010
12
1
327
335
Microwave technique applied to the hydrothermal synthesis and sintering of calcia stabilized zirconia nanoparticles / Rizzuti, A.; Corradi, A.; Leonelli, C.; Rosa, R.; Pielaszek, R.; Lojkowski, W.. - In: JOURNAL OF NANOPARTICLE RESEARCH. - ISSN 1388-0764. - 12:1(2010), pp. 327-335. [10.1007/s11051-009-9619-9]
Rizzuti, A.; Corradi, A.; Leonelli, C.; Rosa, R.; Pielaszek, R.; Lojkowski, W.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1207800
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 18
  • ???jsp.display-item.citation.isi??? 12
social impact