45S5 bioactive glass-polycaprolactone composite porous scaffolds were produced using a solution blending and salt-leaching technique. The main target was the optimisation of the fabrication parameters (such as: blending conditions; nature and amount of salt; glass weight fraction and granulometric size distribution) in order to confer a suitable porosity and composition to the composite scaffold.

Fabrication of 45S5 bioactive glass-polycaprolactone composite scaffolds / Cannillo, V.; Fabbri, P.; Sola, A.. - (2009). (Intervento presentato al convegno 17th International Conference on Composite Materials (ICCM-17) tenutosi a Edinburgh, UK nel 27-31 July 2009).

Fabrication of 45S5 bioactive glass-polycaprolactone composite scaffolds

Cannillo V.;Sola A.
2009

Abstract

45S5 bioactive glass-polycaprolactone composite porous scaffolds were produced using a solution blending and salt-leaching technique. The main target was the optimisation of the fabrication parameters (such as: blending conditions; nature and amount of salt; glass weight fraction and granulometric size distribution) in order to confer a suitable porosity and composition to the composite scaffold.
2009
17th International Conference on Composite Materials (ICCM-17)
Edinburgh, UK
27-31 July 2009
Cannillo, V.; Fabbri, P.; Sola, A.
Fabrication of 45S5 bioactive glass-polycaprolactone composite scaffolds / Cannillo, V.; Fabbri, P.; Sola, A.. - (2009). (Intervento presentato al convegno 17th International Conference on Composite Materials (ICCM-17) tenutosi a Edinburgh, UK nel 27-31 July 2009).
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1203539
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 3
  • ???jsp.display-item.citation.isi??? ND
social impact