The phosphors of formula Ba5Si8O21:Eu2+,Dy3+ were synthesized and studied in order to improve their properties. Their synthesis conditions were evaluated as a function of precursors, crucible composition, flux agents, dopants and temperatures. The samples were characterised by means of a systematic investigation through elemental, kinetic, mineralogical (both qualitative and quantitative), and morphological analysis. This study allows for a careful evaluation of the parameters that influence the formation and properties of Ba5Si8O21:Eu2+,Dy3+ phosphors. As for the synthesis conditions, the use of Na2SiO3, BaCO3 and NH4Cl as precursors was very important to reduce the temperature and time of synthesis. The reducing atmosphere produced with purified coal was cheaper and gave results similar to the more traditional gas mixture (H2/N2). At the end of this study, a phosphor with improved long persistent phosphorescence (LPP) characteristics was obtained with Ba/Si = 0.7, Eu/Si = 2.8 × 10−3 and Dy/Si = 3.6 × 10−3 following a 6 h-synthesis in a quartz crucible
Preparation and Luminescence Properties of Ba5Si8O21 Long Persistent Phosphors Doped with Rare-Earth Elements / Silvestri, Andrea; Ligabue, MARIA LAURA; Malavasi, Gianluca; Lusvardi, Gigliola. - In: MATERIALS. - ISSN 1996-1944. - (2019), pp. 1-12. [10.3390/ma12010183]
Preparation and Luminescence Properties of Ba5Si8O21 Long Persistent Phosphors Doped with Rare-Earth Elements
Maria Laura Ligabue;Gianluca Malavasi;Gigliola Lusvardi
2019
Abstract
The phosphors of formula Ba5Si8O21:Eu2+,Dy3+ were synthesized and studied in order to improve their properties. Their synthesis conditions were evaluated as a function of precursors, crucible composition, flux agents, dopants and temperatures. The samples were characterised by means of a systematic investigation through elemental, kinetic, mineralogical (both qualitative and quantitative), and morphological analysis. This study allows for a careful evaluation of the parameters that influence the formation and properties of Ba5Si8O21:Eu2+,Dy3+ phosphors. As for the synthesis conditions, the use of Na2SiO3, BaCO3 and NH4Cl as precursors was very important to reduce the temperature and time of synthesis. The reducing atmosphere produced with purified coal was cheaper and gave results similar to the more traditional gas mixture (H2/N2). At the end of this study, a phosphor with improved long persistent phosphorescence (LPP) characteristics was obtained with Ba/Si = 0.7, Eu/Si = 2.8 × 10−3 and Dy/Si = 3.6 × 10−3 following a 6 h-synthesis in a quartz crucibleFile | Dimensione | Formato | |
---|---|---|---|
materials-12-00183-v2.pdf
Open access
Tipologia:
VOR - Versione pubblicata dall'editore
Dimensione
3.59 MB
Formato
Adobe PDF
|
3.59 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris