Calcite-based composite scaffolds have been successfully 3D-printed by direct ink writing, starting from a paste comprising a silicone polymer and calcite (CaCO3) powders. The firing in nitrogen, at 600 °C, after preliminary cross-linking step at 350 °C, determined the transformation of the polymer matrix into a silica-carbon nano-composite, embedding unreacted calcite particles. Compared to previously developed silica-calcite scaffolds, obtained after firing in air, the new composites exhibited a significant strength improvement (up to ∼10 MPa, for a total open porosity of 56%). The new formulation did not compromise the in vitro bioactivity and the biocompatibility of the scaffolds, as shown by dissolution studies in SBF and preliminary cell culture tests, with human fibroblasts. Due to the simplicity of the processing and the outstanding mechanical performances, the developed scaffolds are promising candidates for bone tissue engineering applications.

Direct ink writing of silica-carbon-calcite composite scaffolds from a silicone resin and fillers / Elsayed, Hamada; Carraro, Francesco; Agnoli, Stefano; Bellucci, Devis; Cannillo, Valeria; Ferroni, Letizia; Gardin, Chiara; Zavan, Barbara; Bernardo, Enrico. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - 38:15(2018), pp. 5200-5207. [10.1016/j.jeurceramsoc.2018.07.049]

Direct ink writing of silica-carbon-calcite composite scaffolds from a silicone resin and fillers

Bellucci, Devis;Cannillo, Valeria;
2018

Abstract

Calcite-based composite scaffolds have been successfully 3D-printed by direct ink writing, starting from a paste comprising a silicone polymer and calcite (CaCO3) powders. The firing in nitrogen, at 600 °C, after preliminary cross-linking step at 350 °C, determined the transformation of the polymer matrix into a silica-carbon nano-composite, embedding unreacted calcite particles. Compared to previously developed silica-calcite scaffolds, obtained after firing in air, the new composites exhibited a significant strength improvement (up to ∼10 MPa, for a total open porosity of 56%). The new formulation did not compromise the in vitro bioactivity and the biocompatibility of the scaffolds, as shown by dissolution studies in SBF and preliminary cell culture tests, with human fibroblasts. Due to the simplicity of the processing and the outstanding mechanical performances, the developed scaffolds are promising candidates for bone tissue engineering applications.
2018
38
15
5200
5207
Direct ink writing of silica-carbon-calcite composite scaffolds from a silicone resin and fillers / Elsayed, Hamada; Carraro, Francesco; Agnoli, Stefano; Bellucci, Devis; Cannillo, Valeria; Ferroni, Letizia; Gardin, Chiara; Zavan, Barbara; Bernardo, Enrico. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - 38:15(2018), pp. 5200-5207. [10.1016/j.jeurceramsoc.2018.07.049]
Elsayed, Hamada; Carraro, Francesco; Agnoli, Stefano; Bellucci, Devis; Cannillo, Valeria; Ferroni, Letizia; Gardin, Chiara; Zavan, Barbara; Bernardo, ...espandi
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1167192
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 20
  • ???jsp.display-item.citation.isi??? 14
social impact