Laser-based powder bed fusion (L-PBF) is nowadays the preeminent additive manufacturing (AM) technique to produce metal parts. Nonetheless, relatively few metal powders are currently available for industrial L-PBF, especially if aluminum-based feedstocks are involved. In order to fill the existing gap, A357.0 (also known as A357 or A13570) powders are here processed by L-PBF and, for the first time, the fatigue behavior is investigated in the as-built state to verify the net-shaping potentiality of AM. Both the low-cycle and high-cycle fatigue areas are analyzed to draw the complete Wohler diagram. The infinite lifetime limit is set to 2 × 106stress cycles and the staircase method is applied to calculate a mean fatigue strength of 60 MPa. This value is slightly lower but still comparable to the published data for AlSi10Mg parts manufactured by L-PBF, even if the A357.0 samples considered here have not received any post-processing treatment.
Fatigue behavior of as-built L-PBF A357.0 parts / Bassoli, Elena; Denti, Lucia; Comin, Andrea; Sola, Antonella; Tognoli, Emanuele. - In: METALS. - ISSN 2075-4701. - 8:8(2018), pp. N/A-N/A. [10.3390/met8080634]
Fatigue behavior of as-built L-PBF A357.0 parts
Bassoli, Elena;Denti, Lucia;Sola, Antonella;Tognoli, Emanuele
2018
Abstract
Laser-based powder bed fusion (L-PBF) is nowadays the preeminent additive manufacturing (AM) technique to produce metal parts. Nonetheless, relatively few metal powders are currently available for industrial L-PBF, especially if aluminum-based feedstocks are involved. In order to fill the existing gap, A357.0 (also known as A357 or A13570) powders are here processed by L-PBF and, for the first time, the fatigue behavior is investigated in the as-built state to verify the net-shaping potentiality of AM. Both the low-cycle and high-cycle fatigue areas are analyzed to draw the complete Wohler diagram. The infinite lifetime limit is set to 2 × 106stress cycles and the staircase method is applied to calculate a mean fatigue strength of 60 MPa. This value is slightly lower but still comparable to the published data for AlSi10Mg parts manufactured by L-PBF, even if the A357.0 samples considered here have not received any post-processing treatment.File | Dimensione | Formato | |
---|---|---|---|
metals-08-00634.pdf
Open access
Tipologia:
Versione pubblicata dall'editore
Dimensione
2.71 MB
Formato
Adobe PDF
|
2.71 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris