The effect of process parameters on the creep-fatigue behavior of a hot-work tool steel for aluminum extrusion die was investigated through a technological test in which the specimen geometry resembled the mandrel of a hollow extrusion die. Tests were performed on a Gleeble thermomechanical simulator by heating the specimen using joule’s effect and by applying cyclic loading up to 6.30 h or till specimen failure. Displacements during the tests at 380, 490, 540 and 580°C and under the average stresses of 400, 600 and 800 MPa were determined. A dwell time of 3 min was introduced during each of the tests to understand the creep behavior. The results showed that the test could indeed physically simulate the cyclic loading on the hollow die during extrusion and reveal all the mechanisms of creep-fatigue interaction.
Creep-fatigue interaction in the AISI H11 tool steel / Reggiani, Barbara; D'Ascenzo, Marco; Donati, Lorenzo; Jie, Zhou; Tomesani, Luca. - 424:(2010), pp. 205-212. (Intervento presentato al convegno International Conference on Extrusion and Benchmark (ICEB) tenutosi a Dortmund, deu nel 16-17 Settembre 2009) [10.4028/www.scientific.net/KEM.424.205].
Creep-fatigue interaction in the AISI H11 tool steel
Reggiani Barbara;
2010
Abstract
The effect of process parameters on the creep-fatigue behavior of a hot-work tool steel for aluminum extrusion die was investigated through a technological test in which the specimen geometry resembled the mandrel of a hollow extrusion die. Tests were performed on a Gleeble thermomechanical simulator by heating the specimen using joule’s effect and by applying cyclic loading up to 6.30 h or till specimen failure. Displacements during the tests at 380, 490, 540 and 580°C and under the average stresses of 400, 600 and 800 MPa were determined. A dwell time of 3 min was introduced during each of the tests to understand the creep behavior. The results showed that the test could indeed physically simulate the cyclic loading on the hollow die during extrusion and reveal all the mechanisms of creep-fatigue interaction.
| File | Dimensione | Formato | |
|---|---|---|---|
|
KEM_2009_Creep_fatigue_interaction.pdf
Accesso riservato
Tipologia:
Versione pubblicata dall'editore
Dimensione
733.8 kB
Formato
Adobe PDF
|
733.8 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris