The electrophoretic deposition (EPD) was applied to BiFeO3 (BFO) powders, one of the most interesting multiferroic compounds characterized by simultaneous magnetic and ferroelectric activity, to form homogeneous films. The preparation and characterization of stable BFO colloidal suspensions in aqueous, organic and mixed solvents were investigated by zeta potential measurements at room temperature in the presence of surfactants. BFO thin films were then deposited on steel substrates from stabilized BFO suspensions, by adjusting the preparative parameters to optimize the film quality. The compositional, morphological and electrical characteristics of the obtained BFO films, together with thickness measurements, were studied using SEM, XRD, AFM, EIS and optical surface profilometer. EPD method applied to BFO stable suspensions produced homogeneous thickness BFO films, free from pinholes and cracks, that were successively sintered and characterized also in terms of photocatalytic response.
Electrophoretic deposition of multiferroic BiFeO3 sub-micrometric particles from stabilized suspensions / Ponzoni, Chiara; Rosa, Roberto; Cannio, Maria; Buscaglia, Vincenzo; Finocchio, Elisabetta; Nanni, Paolo; Leonelli, Cristina. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - 33:7(2013), pp. 1325-1333. [10.1016/j.jeurceramsoc.2012.12.007]
Electrophoretic deposition of multiferroic BiFeO3 sub-micrometric particles from stabilized suspensions
PONZONI, Chiara;ROSA, Roberto;CANNIO, Maria;LEONELLI, Cristina
2013
Abstract
The electrophoretic deposition (EPD) was applied to BiFeO3 (BFO) powders, one of the most interesting multiferroic compounds characterized by simultaneous magnetic and ferroelectric activity, to form homogeneous films. The preparation and characterization of stable BFO colloidal suspensions in aqueous, organic and mixed solvents were investigated by zeta potential measurements at room temperature in the presence of surfactants. BFO thin films were then deposited on steel substrates from stabilized BFO suspensions, by adjusting the preparative parameters to optimize the film quality. The compositional, morphological and electrical characteristics of the obtained BFO films, together with thickness measurements, were studied using SEM, XRD, AFM, EIS and optical surface profilometer. EPD method applied to BFO stable suspensions produced homogeneous thickness BFO films, free from pinholes and cracks, that were successively sintered and characterized also in terms of photocatalytic response.
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris