The continuous structural transformation of tetragonal analcime (Na15.87Al15.20Si32.64 O-96. 16.3H(2)O) upon dehydration was studied, using Rietveld structure analysis of temperature-resolved powder diffraction data collected using synchrotron radiation. The variation of the a-e axis length difference and normalized intensity of the (200) reflection as a function of temperature suggest that tetragonal analcime evolves toward a cubic structure at high temperature. The removal of water was accompanied by a spreading of the initial Na sites into many positions bonded to the framework O atoms. The migration of H2O molecules through the [111] channels during dehydration caused the six-member ring apertures to open as widely as possible: this was accompanied by a twisting of the tetragonal prism, constituting the analcime framework, which led to an opposite tilting of tetrahedra connecting the prisms. These modifications induced by water diffusion an not energetically favored because they would increase the elastic energy of the system, and require a substantial thermal activation energy. The analcime framework reached a maximum distortion at about 650 K, the temperature of complete water loss, then underwent a relaxation process during which the T-O-T angles were restored to the starting value. The relative variation of cell volume associated with the opening of wide six-member ring channels during water migration, and then due to the framework relaxation process after complete dehydration, provides an explanation of the negative thermal expansion (i.e., volume contraction) effect in dehydrated analcime, which is complementary to that based on the Rigid Unit Modes theory.

Dehydration dynamics of analcime by in situ synchrotron powder diffraction / Cruciani, G; Gualtieri, Alessandro. - In: AMERICAN MINERALOGIST. - ISSN 0003-004X. - 84:(1999), pp. 112-119. [10.2138/am-1999-1-212]

Dehydration dynamics of analcime by in situ synchrotron powder diffraction

GUALTIERI, Alessandro
1999

Abstract

The continuous structural transformation of tetragonal analcime (Na15.87Al15.20Si32.64 O-96. 16.3H(2)O) upon dehydration was studied, using Rietveld structure analysis of temperature-resolved powder diffraction data collected using synchrotron radiation. The variation of the a-e axis length difference and normalized intensity of the (200) reflection as a function of temperature suggest that tetragonal analcime evolves toward a cubic structure at high temperature. The removal of water was accompanied by a spreading of the initial Na sites into many positions bonded to the framework O atoms. The migration of H2O molecules through the [111] channels during dehydration caused the six-member ring apertures to open as widely as possible: this was accompanied by a twisting of the tetragonal prism, constituting the analcime framework, which led to an opposite tilting of tetrahedra connecting the prisms. These modifications induced by water diffusion an not energetically favored because they would increase the elastic energy of the system, and require a substantial thermal activation energy. The analcime framework reached a maximum distortion at about 650 K, the temperature of complete water loss, then underwent a relaxation process during which the T-O-T angles were restored to the starting value. The relative variation of cell volume associated with the opening of wide six-member ring channels during water migration, and then due to the framework relaxation process after complete dehydration, provides an explanation of the negative thermal expansion (i.e., volume contraction) effect in dehydrated analcime, which is complementary to that based on the Rigid Unit Modes theory.
1999
84
112
119
Dehydration dynamics of analcime by in situ synchrotron powder diffraction / Cruciani, G; Gualtieri, Alessandro. - In: AMERICAN MINERALOGIST. - ISSN 0003-004X. - 84:(1999), pp. 112-119. [10.2138/am-1999-1-212]
Cruciani, G; Gualtieri, Alessandro
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/8061
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 73
  • ???jsp.display-item.citation.isi??? 68
social impact