Cross-linked polyethylene (XLPE) films have been coated with nanostructured hybrid organic-inorganic coatings in order to improve their durability. For this purpose, bi- and mono-layer coatings containing different amount of silica and different organic polymers have been prepared through sol-gel reactions and applied to XLPE commercial films. The thermo-oxidative stability, electrical strength and conductivity of XLPE coated films have been investigated after ageing in air at temperatures above the on-service conditions, i.e. at 105 and 120 °C for 1900 and 600 h, respectively. The performed investigations (FT-IR, DSC, TGA and electrical properties) showed that all the coatings tested were able to strongly protect XLPE against oxidation, and that the coating with a PVOH/SiO2 layer gave the best protection. The increase of thermal resistance induced by the coatings reflects on the electrical strength after ageing, which is higher for coated samples than for uncoated ones. Moreover, whileageing has only a slight effect on electrical conductivity in different coated samples, a strong increase of conductivity was observed after ageing for highly oxidated uncoated samples.

Effects of organic-inorganic hybrid coatings on durability of cross-linked polyethylene / Saccani, Andrea; Toselli, Moreno; Pilati, Francesco; Fabiani, Davide; F., Palmieri. - In: POLYMER DEGRADATION AND STABILITY. - ISSN 0141-3910. - STAMPA. - 96:(2011), pp. 2080-2087. [10.1016/j.polymdegradstab.2011.09.023]

Effects of organic-inorganic hybrid coatings on durability of cross-linked polyethylene

SACCANI, Andrea;TOSELLI, MORENO;PILATI, Francesco;FABIANI, Davide;
2011

Abstract

Cross-linked polyethylene (XLPE) films have been coated with nanostructured hybrid organic-inorganic coatings in order to improve their durability. For this purpose, bi- and mono-layer coatings containing different amount of silica and different organic polymers have been prepared through sol-gel reactions and applied to XLPE commercial films. The thermo-oxidative stability, electrical strength and conductivity of XLPE coated films have been investigated after ageing in air at temperatures above the on-service conditions, i.e. at 105 and 120 °C for 1900 and 600 h, respectively. The performed investigations (FT-IR, DSC, TGA and electrical properties) showed that all the coatings tested were able to strongly protect XLPE against oxidation, and that the coating with a PVOH/SiO2 layer gave the best protection. The increase of thermal resistance induced by the coatings reflects on the electrical strength after ageing, which is higher for coated samples than for uncoated ones. Moreover, whileageing has only a slight effect on electrical conductivity in different coated samples, a strong increase of conductivity was observed after ageing for highly oxidated uncoated samples.
2011
96
2080
2087
Effects of organic-inorganic hybrid coatings on durability of cross-linked polyethylene / Saccani, Andrea; Toselli, Moreno; Pilati, Francesco; Fabiani, Davide; F., Palmieri. - In: POLYMER DEGRADATION AND STABILITY. - ISSN 0141-3910. - STAMPA. - 96:(2011), pp. 2080-2087. [10.1016/j.polymdegradstab.2011.09.023]
Saccani, Andrea; Toselli, Moreno; Pilati, Francesco; Fabiani, Davide; F., Palmieri
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/706536
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 9
  • ???jsp.display-item.citation.isi??? 8
social impact