We studied the Co/Fe bi- and multilayer growth on Fe single crystal using the primary-beam diffraction modulated electron emission (PDMEE) technique. This approach enables a chemical selected structural characterization of both surface and buried layers and interfaces to be performed. Co growth on the Fe(001) surface was studied in the 3–70 ML coverage range. The transition from the initial epitaxial bcc phase of the Co film to the stable hcp phase was found to occur rather abruptly at 25–30 ML coverage, a value larger than previously reported in the literature. Subsequent Fe deposition on the Co hcp film recovers the bcc structure in the sandwiched Co layer. However, removal of the Fe epilayer by mild sputtering results again in an hcp Co film.
Surface and near surface structure of Fe-Co layers by scattering-interference of primary electrons / G. C., Gazzadi; A., di Bona; F., Borgatti; Rota, Alberto; Valeri, Sergio. - In: SURFACE REVIEW AND LETTERS. - ISSN 0218-625X. - ELETTRONICO. - 4-6:(1997), pp. 1267-1271.
Surface and near surface structure of Fe-Co layers by scattering-interference of primary electrons
ROTA, Alberto;VALERI, Sergio
1997
Abstract
We studied the Co/Fe bi- and multilayer growth on Fe single crystal using the primary-beam diffraction modulated electron emission (PDMEE) technique. This approach enables a chemical selected structural characterization of both surface and buried layers and interfaces to be performed. Co growth on the Fe(001) surface was studied in the 3–70 ML coverage range. The transition from the initial epitaxial bcc phase of the Co film to the stable hcp phase was found to occur rather abruptly at 25–30 ML coverage, a value larger than previously reported in the literature. Subsequent Fe deposition on the Co hcp film recovers the bcc structure in the sandwiched Co layer. However, removal of the Fe epilayer by mild sputtering results again in an hcp Co film.
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris