The Cleaned cathode ray tube (CRT) glass comes from the dismantling plant of TV and PC color kinescopes and has been used to completely replace both feldspathic and inert components of a traditional ceramic body. Panel glass has been added (up to 20 wt%) to a mixture of two commercial ball clays in order to obtain laboratory tiles sintered at 12101C. Densification has been studied according to ISO rules, while sinterability has been estimated by optical dilatometry. The samples obtained showed main properties similar to commercial ceramic floor and/or wall tiles.
The cleaned cathode ray tube (CRT) glass comes from the dismantling plant of TV and PC color kinescopes and has been used to completely replace both feldspathic and inert components of a traditional ceramic body. Panel glass has been added (up to 20 wt%) to a mixture of two commercial ball clays in order to obtain laboratory tiles sintered at 1210 degrees C. Densification has been studied according to ISO rules, while sinterability has been estimated by optical dilatometry. The samples obtained showed main properties similar to commercial ceramic floor and/or wall tiles.
Recycling of screen glass into new traditional ceramics materials / Andreola, Nora Maria; Barbieri, Luisa; F., Bondioli; Lancellotti, Isabella; Miselli, Paola; Ferrari, Anna Maria. - In: INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY. - ISSN 1546-542X. - STAMPA. - 7:6(2010), pp. 909-917. [10.1111/j.1744-7402.2009.02378.x]
Recycling of screen glass into new traditional ceramics materials
ANDREOLA, Nora Maria;BARBIERI, Luisa;LANCELLOTTI, Isabella;MISELLI, Paola;FERRARI, Anna Maria
2010
Abstract
The cleaned cathode ray tube (CRT) glass comes from the dismantling plant of TV and PC color kinescopes and has been used to completely replace both feldspathic and inert components of a traditional ceramic body. Panel glass has been added (up to 20 wt%) to a mixture of two commercial ball clays in order to obtain laboratory tiles sintered at 1210 degrees C. Densification has been studied according to ISO rules, while sinterability has been estimated by optical dilatometry. The samples obtained showed main properties similar to commercial ceramic floor and/or wall tiles.
| File | Dimensione | Formato | |
|---|---|---|---|
|
Int J Applied Ceramic Tech - 2013 - Andreola - Recycling of Screen Glass Into New Traditional Ceramic Materials.pdf
Accesso riservato
Tipologia:
Versione pubblicata dall'editore
Dimensione
325.76 kB
Formato
Adobe PDF
|
325.76 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris