FePt thin films were epitaxially grown by RF sputtering on MgO (1 0 0) substrates at 550 1C, followed by in situ annealing at the sametemperature. The in situ annealing was found to improve the magnetic characteristics: i.e., the increase in magnetic squareness up to 0.9and increase in the ratio between anisotropy and coercivity (e ¼ anisotropy field/coercive field ¼ 35.9 for 115 min annealing).Remarkably, a decrease in grain size was also found to occur by increasing the annealing time.r 2007 Elsevier B.V. All rights reserved.

Grain size reduction and magnetic properties improvement by in-situ annealing of FePt epitaxial thin films / F., Albertini; L., Nasi; F., Casoli; S., Fabbrici; P., Luches; Rota, Alberto; Valeri, Sergio. - In: JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS. - ISSN 0304-8853. - STAMPA. - 316:2(2007), pp. e158-e161. [10.1016/j.jmmm.2007.02.074]

Grain size reduction and magnetic properties improvement by in-situ annealing of FePt epitaxial thin films

ROTA, Alberto;VALERI, Sergio
2007

Abstract

FePt thin films were epitaxially grown by RF sputtering on MgO (1 0 0) substrates at 550 1C, followed by in situ annealing at the sametemperature. The in situ annealing was found to improve the magnetic characteristics: i.e., the increase in magnetic squareness up to 0.9and increase in the ratio between anisotropy and coercivity (e ¼ anisotropy field/coercive field ¼ 35.9 for 115 min annealing).Remarkably, a decrease in grain size was also found to occur by increasing the annealing time.r 2007 Elsevier B.V. All rights reserved.
2007
316
2
e158
e161
Grain size reduction and magnetic properties improvement by in-situ annealing of FePt epitaxial thin films / F., Albertini; L., Nasi; F., Casoli; S., Fabbrici; P., Luches; Rota, Alberto; Valeri, Sergio. - In: JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS. - ISSN 0304-8853. - STAMPA. - 316:2(2007), pp. e158-e161. [10.1016/j.jmmm.2007.02.074]
F., Albertini; L., Nasi; F., Casoli; S., Fabbrici; P., Luches; Rota, Alberto; Valeri, Sergio
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/586009
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 12
  • ???jsp.display-item.citation.isi??? 11
social impact