Monodispersed silica colloidal spherical nanoparticles were synthesized from the hydrolysis and condensation of tetraethylorthosilicate (TEOS) by using a continuous microwave synthesis process. The flow rate was varied from 43 to 101mL/min in order to establish the optimum conditions required to obtain unagglomerated silica nanopowders. The results were compared with those obtained in batch systems.In particular the mean particle diameter became smaller than 50 nm as the residence time was decreased by increasing the flow rate to 101mL/min.

Synthesis of Silica Nanoparticles in a Continuous-Flow Microwave Reactor / A., Corradi; F., Bondioli; Ferrari, Anna Maria; B., Focher; Leonelli, Cristina. - In: POWDER TECHNOLOGY. - ISSN 0032-5910. - STAMPA. - 167:1(2006), pp. 45-48. [10.1016/j.powtec.2006.05.009]

Synthesis of Silica Nanoparticles in a Continuous-Flow Microwave Reactor

FERRARI, Anna Maria;LEONELLI, Cristina
2006

Abstract

Monodispersed silica colloidal spherical nanoparticles were synthesized from the hydrolysis and condensation of tetraethylorthosilicate (TEOS) by using a continuous microwave synthesis process. The flow rate was varied from 43 to 101mL/min in order to establish the optimum conditions required to obtain unagglomerated silica nanopowders. The results were compared with those obtained in batch systems.In particular the mean particle diameter became smaller than 50 nm as the residence time was decreased by increasing the flow rate to 101mL/min.
2006
167
1
45
48
Synthesis of Silica Nanoparticles in a Continuous-Flow Microwave Reactor / A., Corradi; F., Bondioli; Ferrari, Anna Maria; B., Focher; Leonelli, Cristina. - In: POWDER TECHNOLOGY. - ISSN 0032-5910. - STAMPA. - 167:1(2006), pp. 45-48. [10.1016/j.powtec.2006.05.009]
A., Corradi; F., Bondioli; Ferrari, Anna Maria; B., Focher; Leonelli, Cristina
File in questo prodotto:
File Dimensione Formato  
2006_Powder Technology 167 45–48.pdf

Accesso riservato

Tipologia: Versione pubblicata dall'editore
Dimensione 240.35 kB
Formato Adobe PDF
240.35 kB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/454153
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 67
  • ???jsp.display-item.citation.isi??? 56
social impact