Titania nanoparticles were prepared by means of two different synthetic procedures in order to obtain different particle size (diameter ranging from 20 nm to 350 nm), shapes and morphologies (amorphous or crystalline). Titania nanoparticles were surface modified with octadecylsilane in order to improve their compatibility with respect to polymeric matrices. High density polyethylene (HDPE) - titania nanocomposites were prepared by melt blending by using an internal mixer. The obtained nanocomposites were mechanically characterized and quasi static and creep tensile conditions. The presence of titania nanoparticles (1%vol) led to a significant increase of elastic modulus (20-25%) together with a slight increase of yield stress and a decrease of ultimate elongation. An interesting reduction of for both elastic and viscoelastic creep compliance components was also evidenced.

High-density polyethylene reinforced with titania nanoparticles / Bondioli, Federica; Dorigato, A; Fabbri, Paola; Messori, Massimo; Pegoretti, A.. - In: POLYMER ENGINEERING AND SCIENCE. - ISSN 0032-3888. - STAMPA. - 48[3]:(2008), pp. 448-457.

High-density polyethylene reinforced with titania nanoparticles

BONDIOLI, Federica;FABBRI, Paola;MESSORI, Massimo;
2008

Abstract

Titania nanoparticles were prepared by means of two different synthetic procedures in order to obtain different particle size (diameter ranging from 20 nm to 350 nm), shapes and morphologies (amorphous or crystalline). Titania nanoparticles were surface modified with octadecylsilane in order to improve their compatibility with respect to polymeric matrices. High density polyethylene (HDPE) - titania nanocomposites were prepared by melt blending by using an internal mixer. The obtained nanocomposites were mechanically characterized and quasi static and creep tensile conditions. The presence of titania nanoparticles (1%vol) led to a significant increase of elastic modulus (20-25%) together with a slight increase of yield stress and a decrease of ultimate elongation. An interesting reduction of for both elastic and viscoelastic creep compliance components was also evidenced.
2008
48[3]
448
457
High-density polyethylene reinforced with titania nanoparticles / Bondioli, Federica; Dorigato, A; Fabbri, Paola; Messori, Massimo; Pegoretti, A.. - In: POLYMER ENGINEERING AND SCIENCE. - ISSN 0032-3888. - STAMPA. - 48[3]:(2008), pp. 448-457.
Bondioli, Federica; Dorigato, A; Fabbri, Paola; Messori, Massimo; Pegoretti, A.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/421315
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact