Zirconia nanopowders obtaneid by hydrothermal synthesis were tested in vitro at 60°C for 30 days.Elemental analysis,XRD,SEM,TEM techniques were used for this study.Crystallinity and phase identification was performed before and after in vitro test

In vitro bioactivity testing of ZrO2 nanopowders prepared by MW-assisted hydrothermal synthesis / Bondioli, Federica; Braccini, Silvia; Leonelli, Cristina; Pellacani, Gian Carlo; Lusvardi, Gigliola; Malavasi, Gianluca. - ELETTRONICO. - (2003), pp. 338-341.

In vitro bioactivity testing of ZrO2 nanopowders prepared by MW-assisted hydrothermal synthesis

BONDIOLI, Federica;BRACCINI, Silvia;LEONELLI, Cristina;PELLACANI, Gian Carlo;LUSVARDI, Gigliola;MALAVASI, Gianluca
2003

Abstract

Zirconia nanopowders obtaneid by hydrothermal synthesis were tested in vitro at 60°C for 30 days.Elemental analysis,XRD,SEM,TEM techniques were used for this study.Crystallinity and phase identification was performed before and after in vitro test
2003
Physics, Chemistry and Application of Nanostructures: Rewiews and short notes to Nanomeeting 2003
9789812383815
V.E.Borisenko,S.V.Gaponenko, V.S.Gurin.
GIAPPONE
In vitro bioactivity testing of ZrO2 nanopowders prepared by MW-assisted hydrothermal synthesis / Bondioli, Federica; Braccini, Silvia; Leonelli, Cristina; Pellacani, Gian Carlo; Lusvardi, Gigliola; Malavasi, Gianluca. - ELETTRONICO. - (2003), pp. 338-341.
Bondioli, Federica; Braccini, Silvia; Leonelli, Cristina; Pellacani, Gian Carlo; Lusvardi, Gigliola; Malavasi, Gianluca
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/308398
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact