Magnetic susceptibility from 300 to 900 K, room temperature hysteresis cycles and saturation magnetization were investigated in screen printed and fired NiCo-based layers prepared at various peak temperatures. A bulk NiCo metal sheet of comparable composition was also studied. Values of the magnetic polarization J of 0.28 and 0.435 T were obtained (at 200 kA/m) for films prepared at 750 and 950 degrees C, respectively, in contrast with J = 0.98 T for the bulk alloy. In addition, the magnetoresistive responses of the layers and the sheet were plotted. These data suggest that strains, pores and lack of composition homogeneity in the films concur in affecting their magnetic properties, and are responsible for their reduced magnetoresistance anisotropy (e.g. ca. 4% for films as compared to ca. 8% for the bulk alloy at H = 80 kA/m). (C) 1999 Elsevier Science S.A. All rights reserved.

Magnetic properties of Ni-Co thick-film magnetoresistors / A., Masoero; Morten, Bruno; Gl, Olcese; Prudenziati, Maria; F., Tango; F., Vinai. - In: THIN SOLID FILMS. - ISSN 0040-6090. - STAMPA. - 350:(1999), pp. 214-218.

Magnetic properties of Ni-Co thick-film magnetoresistors

MORTEN, Bruno;PRUDENZIATI, Maria;
1999

Abstract

Magnetic susceptibility from 300 to 900 K, room temperature hysteresis cycles and saturation magnetization were investigated in screen printed and fired NiCo-based layers prepared at various peak temperatures. A bulk NiCo metal sheet of comparable composition was also studied. Values of the magnetic polarization J of 0.28 and 0.435 T were obtained (at 200 kA/m) for films prepared at 750 and 950 degrees C, respectively, in contrast with J = 0.98 T for the bulk alloy. In addition, the magnetoresistive responses of the layers and the sheet were plotted. These data suggest that strains, pores and lack of composition homogeneity in the films concur in affecting their magnetic properties, and are responsible for their reduced magnetoresistance anisotropy (e.g. ca. 4% for films as compared to ca. 8% for the bulk alloy at H = 80 kA/m). (C) 1999 Elsevier Science S.A. All rights reserved.
1999
350
214
218
Magnetic properties of Ni-Co thick-film magnetoresistors / A., Masoero; Morten, Bruno; Gl, Olcese; Prudenziati, Maria; F., Tango; F., Vinai. - In: THIN SOLID FILMS. - ISSN 0040-6090. - STAMPA. - 350:(1999), pp. 214-218.
A., Masoero; Morten, Bruno; Gl, Olcese; Prudenziati, Maria; F., Tango; F., Vinai
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/306085
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 14
  • ???jsp.display-item.citation.isi??? 12
social impact