Degradation of yttria-stabilized zirconia (YSZ) layers by molten CaO-MgO-Al2O3-SiO2 (CMAS)-based deposits is an important failure mode of thermal barrier coating (TBC) systems in modern gas turbines. The present work aimed to understand how the chemical purity and microstructure of plasma-sprayed YSZ layers affect their response to CMAS corrosion. To this end, isothermal corrosion tests (1 h at 1250 °C) were performed on four different kinds of YSZ coatings: atmospheric plasma-sprayed (APS) layers obtained from standard- and high-purity feedstock powders, a dense – vertically cracked (DVC) layer, and a suspension plasma sprayed (SPS) one. Characterization of corroded and non-corroded samples by FEG-SEM, EBSD and micro-Raman spectroscopy techniques reveals that, whilst all YSZ samples suffered grain-boundary corrosion by molten CMAS, its extent could vary considerably. High chemical purity limits the extent of grain-boundary dissolution by molten CMAS, whereas high porosity and/or fine crystalline grain structure lead to more severe degradation.

CMAS corrosion of YSZ thermal barrier coatings obtained by different thermal spray processes / Morelli, S.; Testa, V.; Bolelli, G.; Ligabue, O.; Molinari, E.; Antolotti, N.; Lusvarghi, L.. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - 40:12(2020), pp. 4084-4100. [10.1016/j.jeurceramsoc.2020.04.058]

CMAS corrosion of YSZ thermal barrier coatings obtained by different thermal spray processes

Morelli S.
Writing – Original Draft Preparation
;
Testa V.
Investigation
;
Bolelli G.
Writing – Original Draft Preparation
;
Molinari E.
Investigation
;
Lusvarghi L.
Writing – Review & Editing
2020

Abstract

Degradation of yttria-stabilized zirconia (YSZ) layers by molten CaO-MgO-Al2O3-SiO2 (CMAS)-based deposits is an important failure mode of thermal barrier coating (TBC) systems in modern gas turbines. The present work aimed to understand how the chemical purity and microstructure of plasma-sprayed YSZ layers affect their response to CMAS corrosion. To this end, isothermal corrosion tests (1 h at 1250 °C) were performed on four different kinds of YSZ coatings: atmospheric plasma-sprayed (APS) layers obtained from standard- and high-purity feedstock powders, a dense – vertically cracked (DVC) layer, and a suspension plasma sprayed (SPS) one. Characterization of corroded and non-corroded samples by FEG-SEM, EBSD and micro-Raman spectroscopy techniques reveals that, whilst all YSZ samples suffered grain-boundary corrosion by molten CMAS, its extent could vary considerably. High chemical purity limits the extent of grain-boundary dissolution by molten CMAS, whereas high porosity and/or fine crystalline grain structure lead to more severe degradation.
2020
40
12
4084
4100
CMAS corrosion of YSZ thermal barrier coatings obtained by different thermal spray processes / Morelli, S.; Testa, V.; Bolelli, G.; Ligabue, O.; Molinari, E.; Antolotti, N.; Lusvarghi, L.. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - 40:12(2020), pp. 4084-4100. [10.1016/j.jeurceramsoc.2020.04.058]
Morelli, S.; Testa, V.; Bolelli, G.; Ligabue, O.; Molinari, E.; Antolotti, N.; Lusvarghi, L.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1207069
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 53
  • ???jsp.display-item.citation.isi??? 44
social impact