A357.0 parts are processed by laser-based powder bed fusion and surface finished via plastic media blasting, ceramic sand blasting, and laser shock processing. The morphological analysis proves that plastic media blasting causes the most effective peak removal, the most efficient decrease in valley depth, and the greatest reduction in surface roughness. All the surface finishing processes enhance the fatigue life, however ceramic sand blasting bring about the greatest increase in the value of σmax for an infinite fatigue life limit of 2106 cycles. The experimental results suggest therefore that the infinite fatigue life value is more sensitive to the residual stress state engendered by ceramic sand blasting than to the reduction in surface roughness. Breakthrough cracks start at the interface between crushed or modified surface particles and the underlying macro-surface. However, at a distance of a few hundred microns from the crack initiation point, the fracture surface morphology become cellular for all the specimens.

Effect of Three Different Finishing Processes on the Surface Morphology and Fatigue Life of A357.0 Parts Produced by Laser‐Based Powder Bed Fusion / Gatto, Andrea; Bassoli, Elena; Denti, Lucia; Sola, Antonella; Tognoli, Emanuele; Comin, Andrea; Porro, Juan Antonio; Cordovilla, Francisco; Angulo, Ignacio; Ocaña, Jose Luis. - In: ADVANCED ENGINEERING MATERIALS. - ISSN 1527-2648. - (2019), pp. 1-10. [10.1002/adem.201801357]

Effect of Three Different Finishing Processes on the Surface Morphology and Fatigue Life of A357.0 Parts Produced by Laser‐Based Powder Bed Fusion

Gatto, Andrea;Bassoli, Elena;Denti, Lucia;Sola, Antonella;Tognoli, Emanuele;
2019

Abstract

A357.0 parts are processed by laser-based powder bed fusion and surface finished via plastic media blasting, ceramic sand blasting, and laser shock processing. The morphological analysis proves that plastic media blasting causes the most effective peak removal, the most efficient decrease in valley depth, and the greatest reduction in surface roughness. All the surface finishing processes enhance the fatigue life, however ceramic sand blasting bring about the greatest increase in the value of σmax for an infinite fatigue life limit of 2106 cycles. The experimental results suggest therefore that the infinite fatigue life value is more sensitive to the residual stress state engendered by ceramic sand blasting than to the reduction in surface roughness. Breakthrough cracks start at the interface between crushed or modified surface particles and the underlying macro-surface. However, at a distance of a few hundred microns from the crack initiation point, the fracture surface morphology become cellular for all the specimens.
2019
1
10
Effect of Three Different Finishing Processes on the Surface Morphology and Fatigue Life of A357.0 Parts Produced by Laser‐Based Powder Bed Fusion / Gatto, Andrea; Bassoli, Elena; Denti, Lucia; Sola, Antonella; Tognoli, Emanuele; Comin, Andrea; Porro, Juan Antonio; Cordovilla, Francisco; Angulo, Ignacio; Ocaña, Jose Luis. - In: ADVANCED ENGINEERING MATERIALS. - ISSN 1527-2648. - (2019), pp. 1-10. [10.1002/adem.201801357]
Gatto, Andrea; Bassoli, Elena; Denti, Lucia; Sola, Antonella; Tognoli, Emanuele; Comin, Andrea; Porro, Juan Antonio; Cordovilla, Francisco; Angulo, Ignacio; Ocaña, Jose Luis
File in questo prodotto:
File Dimensione Formato  
Gatto_et_al-2019-Advanced_Engineering_Materials.pdf

Accesso riservato

Descrizione: Articolo principale
Tipologia: Versione pubblicata dall'editore
Dimensione 7.01 MB
Formato Adobe PDF
7.01 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1175641
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 15
  • ???jsp.display-item.citation.isi??? 16
social impact