This paper reports a study, performed by in-situ synchrotron X-ray powder diffraction, of the high-pressure behavior of zeolite L. The experiments were performed using both penetrating (methanol: ethanol: water mixture, m.e.w.) and non-penetrating (silicon oil, s.o.) pressure transmitting media (PTM) to study the compressibility and the possible pressure-induced hydration (PIH) of this synthetic zeolite, technologically relevant as host-guest system exploited in numerous application fields. The experiments were performed from Pamb to 6.2 and 6.3 GPa in s.o. and m.e.w., respectively. The crystal structure refinements were performed up to 6.3 GPa and 3.1 GPa for the patterns collected in m.e.w. and s.o., respectively, while the unit cell parameters were determined in the whole pressure range for both media. A strong PIH effect is evident when zeolite L is compressed in m.e.w. and the over-hydration is essentially ascribable to the filling of most the H2O sites, to the appearance of a new H2O site and to the partially filling of the K sites. The over-hydration starts at a very low pressure (0.5 GPa) and the maximum H2O content can be estimated in 31.1 H2O molecules, against the original value of 18. The PIH is completely reversible upon P release. The main difference between the compression behavior of zeolite L in the two media is the higher compressibility in the non-penetrating one, evidenced by ΔV=− 6.3% and −9.9% in m.e.w. and s.o, respectively. Our data are consistent with the general behavior of zeolites compressed with penetrating media, when the intrusion of H2O molecules hinders the effects of the applied pressure. The results of this work are compared with those obtained on a K-gallosilicate with LTL topology, where PIH induces the formation of H2O nanotubes inside the zeolite channel.

Compressibility behavior and pressure-induced over-hydration of zeolite K-AlSi-L / Lara, Gigli; Vezzalini, Maria Giovanna; Simona, Quartieri; Rossella, Arletti; Arletti, Rossella. - In: MICROPOROUS AND MESOPOROUS MATERIALS. - ISSN 1387-1811. - 276:(2019), pp. 160-166. [10.1016/j.micromeso.2018.09.031]

Compressibility behavior and pressure-induced over-hydration of zeolite K-AlSi-L

Giovanna Vezzalini;ARLETTI, Rossella
2019

Abstract

This paper reports a study, performed by in-situ synchrotron X-ray powder diffraction, of the high-pressure behavior of zeolite L. The experiments were performed using both penetrating (methanol: ethanol: water mixture, m.e.w.) and non-penetrating (silicon oil, s.o.) pressure transmitting media (PTM) to study the compressibility and the possible pressure-induced hydration (PIH) of this synthetic zeolite, technologically relevant as host-guest system exploited in numerous application fields. The experiments were performed from Pamb to 6.2 and 6.3 GPa in s.o. and m.e.w., respectively. The crystal structure refinements were performed up to 6.3 GPa and 3.1 GPa for the patterns collected in m.e.w. and s.o., respectively, while the unit cell parameters were determined in the whole pressure range for both media. A strong PIH effect is evident when zeolite L is compressed in m.e.w. and the over-hydration is essentially ascribable to the filling of most the H2O sites, to the appearance of a new H2O site and to the partially filling of the K sites. The over-hydration starts at a very low pressure (0.5 GPa) and the maximum H2O content can be estimated in 31.1 H2O molecules, against the original value of 18. The PIH is completely reversible upon P release. The main difference between the compression behavior of zeolite L in the two media is the higher compressibility in the non-penetrating one, evidenced by ΔV=− 6.3% and −9.9% in m.e.w. and s.o, respectively. Our data are consistent with the general behavior of zeolites compressed with penetrating media, when the intrusion of H2O molecules hinders the effects of the applied pressure. The results of this work are compared with those obtained on a K-gallosilicate with LTL topology, where PIH induces the formation of H2O nanotubes inside the zeolite channel.
2019
29-set-2018
276
160
166
Compressibility behavior and pressure-induced over-hydration of zeolite K-AlSi-L / Lara, Gigli; Vezzalini, Maria Giovanna; Simona, Quartieri; Rossella, Arletti; Arletti, Rossella. - In: MICROPOROUS AND MESOPOROUS MATERIALS. - ISSN 1387-1811. - 276:(2019), pp. 160-166. [10.1016/j.micromeso.2018.09.031]
Lara, Gigli; Vezzalini, Maria Giovanna; Simona, Quartieri; Rossella, Arletti; Arletti, Rossella
File in questo prodotto:
File Dimensione Formato  
Bozze_MICMAT_9130.pdf

Open access

Descrizione: Bozze
Tipologia: Versione dell'autore revisionata e accettata per la pubblicazione
Dimensione 1.34 MB
Formato Adobe PDF
1.34 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Licenza Creative Commons
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11380/1173096
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 11
social impact