The electrical properties of Ru/SrTiO<inf>x</inf>/Ru capacitors have been investigated. Equivalent Oxide Thickness (EOT) of 0.38 nm at 0 V and current density of 10<sup>-7</sup> A cm<sup>-2</sup> at ±1 V and 25 °C meet the sub-20 nm DRAM requirements. Relaxation measurements were performed, indicating acceptable charge loss. Modeling of charge trapping at defect sites based on multi-phonon trap-assisted-tunneling quantitatively well describes leakage and capacitance behavior.
SrTiO<inf>x</inf> for sub-20 nm DRAM technology nodes - Characterization and modeling / Kaczer, B.; Larcher, Luca; Vandelli, Luca; Reisinger, H.; Popovici, M.; Clima, S.; Ji, Z.; Joshi, S.; Swerts, J.; Redolfi, A.; Afanas'Ev, V. V.; Jurczak, M.. - In: MICROELECTRONIC ENGINEERING. - ISSN 0167-9317. - 147:(2015), pp. 126-129. [10.1016/j.mee.2015.04.070]
SrTiOx for sub-20 nm DRAM technology nodes - Characterization and modeling
LARCHER, Luca;VANDELLI, LUCA;
2015
Abstract
The electrical properties of Ru/SrTiO
| File | Dimensione | Formato | |
|---|---|---|---|
|
SrTiOx.pdf
Accesso riservato
Tipologia:
Versione pubblicata dall'editore
Dimensione
1.43 MB
Formato
Adobe PDF
|
1.43 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I metadati presenti in IRIS UNIMORE sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono rilasciati con licenza Attribuzione 4.0 Internazionale (CC BY 4.0), salvo diversa indicazione.
In caso di violazione di copyright, contattare Supporto Iris